Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 27.0 MPa | 3920 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PQ 81 T 10 Polypropylene reinforced with mineral filler Modified PP for injection molding with the content of 10% mineral filler, impact modified. Delivered in black color.Information Provided by Plastcom spol. s r.o. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
Eastman Eastar GN125 Copolyester, Natural
(discontinued **) Eastar Copolyester GN125 is a glycol modified polyethylene terephthalate (PET) that contains an ultraviolet light inhibitor. This product is recommended for indoor applications requiring enhanced co.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
GEHR Plastics PP-30PET-F Polypropylene, 30% PET Fiber Reinforced
(discontinued **) Polypropylene shows a high mechanical strength and a tensile strength, but a low notched impact strength. PP resists stress cracking and it is easy to weld. At minus temperatures it can get brittle... |
|||
Tensile Strength at Break | 27.0 MPa @Temperature 145 °C, Time 2990 sec |
3920 psi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
LG Chemical NBR 6830 High Acrylonitrile Polymer Description: NBR 6830 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6830 is a non staining, medium low moon.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCA875 PPE-TPE Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | after 7days @136°C; UL 1581 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific) LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | >= 27.0 MPa | >= 3920 psi | |
Sibur SKS-30 ARKPN 2nd Group Styrene-Butadiene Rubber (SBR) SBR-1502. For use in the tire industry for production of tire thread and other parts for tires, in rubber technical industry for production of a wide assortment of rubber technical articles, and in.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Europe-Africa-Middle East) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Sumitomo Bakelite North America SI 9002N-1 Silicone Compound Short fibergass reinforced silicone molding compound which offers moderate strength properties, dimensional stability, and excellent long-term thermal stability at elevated temperatures.Information .. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
SCG Chemicals EL-Leneâ„¢ H5840B High Density Polyethylene Blow Molding Key Characteristics:Excellent environmental stress cracking resistance (ESCR)Excellent appearanceOdorlessSafe for food contactGood printabilityRecommended Applications: Bottles for food, juice, sof.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527-2 |
Tisan TISOPLEN® 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength at Break | >= 27.0 MPa | >= 3920 psi | Requirement |
Westlake Plastics Lennite® GUR1050 (Type II) Ultra-high Molecular Weight Polyethylene For Medical Applications Medical grade Lennite UHMWPE is produced from premium resins in accordance with ASTM specification F648 and International Standard ISO 5834-1 for surgical implants. Westlake Plastics' proprietary m.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 1030 T V0 Flame Retardant ABS Acrylonitrile Butadiene StyreneFlame retardant class V0, PBDE free, high thermal resistance, good impact resistance, high gloss, good light resistance, good processabilityInformation provided by Cos.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
Ecomass® 1950ZC84 Stainless Steel Filled Polyamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsStainless Steel Powder Filled Polyamide (PA6/10)Very Good ToughnessInformation provided by Technical Polym.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ HMU 210 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin, black colored, with high stiffness for automotive HVAC and under-the-hood applications.Availability: Africa & Middle East, Asia Pacif.. |
|||
Tensile Strength at Break | 27.0 - 35.0 MPa | 3920 - 5080 psi | ASTM D638 |
Daikin NEOFLON AP-201 PFA Pellets NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Complicated injection molded parts requiring high melt flow to fil.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334M30CL Mica Reinforced Coupled |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO R 527 |
Addiplast Addilene H 560 Polypropylene Homopolymer High heat resistance, detergent stabilized, anti-yellowingInformation provided by Addiplast. |
|||
Tensile Strength at Break | 27.0 - 48.0 MPa | 3920 - 6960 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2850-02 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339M10L Mica Reinforced |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339M20L Mica Reinforced |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339T10L Talc Reinforced |
|||
Tensile Strength at Break | <= 27.0 MPa | <= 3920 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K8020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP CL002 PS (Europe-Africa-Middle East) LNP* LUBRICOMP* CL002 is a compound based on Polystyrene resin containing PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Sumitomo Bakelite North America SI 9002J-1 Silicone Compound SI 9002J-1 is a short fiberglass reinforced silicone molding compound, which offers moderate strength properties, and dimensional stability and excellent long-term thermal stability at elevated temp.. |
|||
Tensile Strength at Break | 27.0 - 48.0 MPa | 3920 - 6960 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2850-07 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |