Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
SABIC M40053S High Density Polyethylene for Injection Molding Product Description: M40053S is a UV stabilized high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to pro.. |
|||
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PP CQX8025 R2 Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
Polykemi AB POLYfill PP EQX10030R UV Polypropylene, Mineral Reinforced, Modified Information provided by Polykemi AB |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 825ES High Impact Polystyrene Grade 825ES is a high impact polystyrene designed for extrusion and hot molding application. It is suited for hot molded deep drawn industrial packages and multilayer shaped sheet production via ex.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ RTA3263EUV Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ RTA3263EUV fractional melt flow, 1,500 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent com.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD801AU PPE-TPE (Asia Pacific) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCD825 PPE-TPE (Asia Pacific) Flexible, very low-migration, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-1 re.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD891B PPE-TPE (Asia Pacific) Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD891B PPE-TPE (Europe-Africa-Middle East) Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched LNP* LUBRICOMP* OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant. |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ASTM D638 |
Solvay Specialty Polymers Hyflon® PFA P450 Perfluoroalkoxy (PFA) Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat res.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 2Z004 ETFE LNP* THERMOCOMP* 2Z004 is a compound based on ETFE resin containing 20% Milled Glass. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Sterigenics Raprex® R200D Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREX® R200D is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp TH0450D LNP* Thermocomp* TH0450D is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl HIPS3191 PS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD891B PPE-TPE Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
Tensile Strength at Break | 21.0 MPa @Treatment Temp. 145 °C, Time 2100 sec |
3050 psi @Treatment Temp. 293 °F, Time 0.583 hour |
Cure; ASTM D412 |
Styron Sprintan® SLR 4602 Solution Styrene Butadiene Rubber (S-SBR) Composition: SPRINTAN® SLR-4602 – Schkopau is manufactured by anionic solution polymerization using an organo-lithium initiator. The product has a medium styrene/high vinyl micro structure a.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
UBE R300 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2 |
Total Lumicene® mPE M 4041 UV Metallocene Polyethylene, Rotomolding Lumicene® mPE M 4041 UV is a new generation metallocene medium density polyethylene with hexene as comonomer.Lumicene® mPE M 4041 UV is intended for the manufacture of rotomolded items.Lumicene® .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2 |
Total PSI 7240 High Impact Polystyrene 7240 is a very high impact polystyrene for the extrusion industry. This grade has been designed to be diluted with crystal polystyrene (such as LACQRENE® 140, 1340 or 1540) at higher levels than c.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Toyobo PELPRENE™ P40H Polyester TPE Features: Polyester TPEInformation provided by Toyobo. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
Tensile Strength at Break | >= 21.0 MPa | >= 3050 psi | ISO R 527 |
Fainplast Compounds HLA 075 Flexible PVC, Insulation for High Temperatures Operating temperature 105°C |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D882 |
3M 25M25X Protective UV Tape 3M™ Protective UV Tape 25M25X is a proprietary, black and white co-extruded polyethylene tape for temporary outdoor and indoor protection of many metals, plastics and glass.Information provided by .. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO R 527 |
Addiplast Addilene J 120 M10 Polypropylene Copolymer Low fluidity for extrusion or injectionInformation provided by Addiplast. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436M40L Mica Reinforced |
|||
Tensile Strength at Break | >= 21.0 MPa @Temperature 23.0 °C |
>= 3050 psi @Temperature 73.4 °F |
ASTM D1708 |
Solvay Specialty Polymers Hyflon® PFA P450 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resista.. |
|||
Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |