LyondellBasell Hifaxâ„¢ RTA3263EUV Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ RTA3263EUV Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ RTA3263EUV fractional melt flow, 1,500 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent combination of rigidity, impact resistance, melt strength, processability and weatherability. It was designed specifically for thermoformed applications. Uses: SheetInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D 638 |
| Elongation at Break | 450 % | 450 % | ASTM D 638 |
| Elongation at Yield | 400 % | 400 % | ASTM D 638 |
| Flexural Modulus | 1.20 GPa | 174 ksi | Tangent, 0.05 in/min; ASTM D790 |
| 1.50 GPa | 218 ksi | Tangent, 0.5 in/min; ASTM D790 | |
| Izod Impact, Notched | 7.501 J/cm | 14.05 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 32.0 J @Temperature -30.0 °C |
23.6 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| Dart Drop, Total Energy | 20.0 J @Temperature -30.0 °C |
14.8 ft-lb @Temperature -22.0 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Tear Strength | 110 kN/m | 630 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 41.0 µm/m-°C @Temperature -30.0 - 100 °C |
22.8 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Brittleness Temperature | -30.0 °C | -22.0 °F | ASTM D746 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-763 Epoxy Prepreg, 3K 2x2 Twill Carbon Reinforced
- Parker Chomerics Tecknit Consil®-A 895 Silver-Aluminum Filled Silicone Elastomer
- Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/30 Polyurethane Casting Elastomer
- Techmer ES HiFill® PA6 L UV (Conditioned)
- Techmer ES HiFill® PA6/6 GF33 UG BK 33% Glass Filled
- Saint-Gobain CHR® SG23-10(R) Primary Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS
- SABIC Innovative Plastics Xenoy® X5630 PC+PET
- A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
- Polimeri Europa SINKRAL PD A630/E ABS, Impact & Heat Stabilized Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved