Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 17.4 MPa | 2530 psi | |
NEU NeuSoft™ 602-50A Ester TPU / SBC blend |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90055 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B8501 Polyvinyl Chloride, Flexible (PVC, Flexible) A flexible Vinyl compound for hose and tubing applications with enhanced physical characteristics.Information provided by PolyOne |
|||
Tensile Strength at Break | 17.4 MPa @Temperature 200 °C, Time 1.21e+6 sec |
2520 psi @Temperature 392 °F, Time 336 hour |
After Dry Heat Aging; ASTM D865 |
Seals Eastern 7130 Fluorocarbon-Elastomer FKM specially for oil & gas service.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 17.4 MPa @Temperature 200 °C, Time 3.60e+6 sec |
2520 psi @Temperature 392 °F, Time 1000 hour |
After Dry Heat Aging; ASTM D865 |
Seals Eastern 7182D Fluorocarbon-Elastomer Formulated AFLAS® high-temperature "sour" oil & gas service. Excellent acid and base resistance.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | ISO R 527 |
Stir SpA AF 93 CZ BL (PVC) Application: Extrusion flame resistant sheath CEI 20-11 type R 2Information provided by STIR SpA |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | ISO R 527 |
Stir SpA AF 95 (PVC) Application: Flame insulation CEI 20-11 type R 2Information provided by STIR SpA |
|||
Tensile Strength at Break | 17.4 MPa | 2530 psi | ASTM D638 |
Teknor Apex APEX® 88-N131M-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | ASTM D638 |
Teknor Apex Terraloy™ BP 18003A Thermoplastic Starch + HIPS Notes: Terraloy™ BP-18003A is a Thermoplastic Starch/HIPS ready-to-process compound that contains up to 30% of TPS renewable content. This compound is intended for injection molding application. P.. |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | |
Daikin DAI-EL G-501NK Fluoroelastomer Terpolymer, Diamine Curable Grade, 68% Fluorine Content Features: Good mechanical characteristics.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 17.4 MPa | 2520 psi | 50 microns film; ASTM D882 |
Arkema Group Orevac® 9307 Y Film EVA-MAH Terpolymer EVA Terpolymers based Main Applications: Extrusion coating Skin packaging adhesive Thermo-adhesive filmsInformation provided by Arkema Group |
|||
Tensile Strength at Break | 17.4 MPa | 2530 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5642 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5642 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 17.4 MPa | 2530 psi | ASTM D638 |
Teknor Apex APEX® 84132 Polyvinyl Chloride, Flexible Notes: 80°C Insulation and Jacketing; RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |