Material Notes:
FKM specially for oil & gas service.Information provided by Seals Eastern, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.92 g/cc
1.92 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 90
>= 90
ASTM D2240, Type A
93
93
AVG; ASTM D2240, Type A
92

@Temperature 200 °C,
Time 252000 sec
 92

@Temperature 392 °F,
Time 70.0 hour
 After Dry Heat Aging; ASTM D865
93

@Temperature 200 °C,
Time 1.21e+6 sec
 93

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
94

@Temperature 200 °C,
Time 3.60e+6 sec
 94

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
94

@Temperature 200 °C,
Time 605000 sec
 94

@Temperature 392 °F,
Time 168 hour
 After Dry Heat Aging; ASTM D865
Tensile Strength at Break >= 17.2 MPa
>= 2500 psi
ASTM D412 Method A
20.7 MPa
3000 psi
AVG; ASTM D412 Method A
13.9 MPa

@Temperature 200 °C,
Time 360000 sec
 2010 psi

@Temperature 392 °F,
Time 100 hour
 After Dry Heat Aging; ASTM D865
17.4 MPa

@Temperature 200 °C,
Time 1.21e+6 sec
 2520 psi

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
17.6 MPa

@Temperature 200 °C,
Time 605000 sec
 2550 psi

@Temperature 392 °F,
Time 168 hour
 After Dry Heat Aging; ASTM D865
18.8 MPa

@Temperature 200 °C,
Time 252000 sec
 2730 psi

@Temperature 392 °F,
Time 70.0 hour
 After Dry Heat Aging; ASTM D865
Tensile Strength, Yield 6.21 MPa
900 psi
AVG Stress at Elongation M25; ASTM D412 Method A
>= 7.58 MPa
>= 1100 psi
Stress at Elongation M50; ASTM D412 Method A
10.3 MPa
1500 psi
AVG Stress at Elongation M50; ASTM D412 Method A
>= 12.1 MPa
>= 1750 psi
Stress at Elongation M100; ASTM D412 Method A
19.3 MPa
2800 psi
AVG Stress at Elongation M100; ASTM D412 Method A
Elongation at Break >= 100 %
>= 100 %
ASTM D412 Method A
105 %
105 %
AVG; ASTM D412 Method A
94.5 %

@Temperature 200 °C,
Time 360000 sec
 94.5 %

@Temperature 392 °F,
Time 100 hour
 After Dry Heat Aging; ASTM D865
94.5 %

@Temperature 200 °C,
Time 605000 sec
 94.5 %

@Temperature 392 °F,
Time 168 hour
 After Dry Heat Aging; ASTM D865
98.7 %

@Temperature 200 °C,
Time 1.21e+6 sec
 98.7 %

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
107.1 %

@Temperature 200 °C,
Time 252000 sec
 107.1 %

@Temperature 392 °F,
Time 70.0 hour
 After Dry Heat Aging; ASTM D865
Modulus of Elasticity 0.03878 GPa
5.625 ksi
ASTM D412 Method A
Shear Modulus 0.01293 GPa
1.875 ksi
ASTM D412 Method A
Secant Modulus 0.03646 GPa
5.288 ksi
ASTM D412 Method A
Tear Strength Test 180
180
(psi); ASTM D624, Die B
Compression Set 12 %

@Temperature 200 °C,
Time 79200 sec
 12 %

@Temperature 392 °F,
Time 22.0 hour
 ASTM D395, Test B
16 %

@Temperature 200 °C,
Time 252000 sec
 16 %

@Temperature 392 °F,
Time 70.0 hour
 ASTM D395, Test B
28 %

@Temperature 200 °C,
Time 1.21e+6 sec
 28 %

@Temperature 392 °F,
Time 336 hour
 ASTM D395, Test B
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
ASTM D1329
Glass Transition Temp, Tg -20.0 °C
-4.00 °F
ASTM D1329
Processing Properties Metric English Comments
Shelf Life 180 Month
180 Month
ASTM D395, Test B
Descriptive Properties Value Comments
Strain Energy / Unit Volume at 20% Elongation (psi) 100