Arkema Group Orevac® 9307 Y Film EVA-MAH Terpolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate |
| Manufacturer | Arkema |
| Trade Name | OREVAC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orevac® 9307 Y Film EVA-MAH Terpolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EVA Terpolymers based Main Applications: Extrusion coating Skin packaging adhesive Thermo-adhesive filmsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 13 - 15 % | 13 - 15 % | |
| Melt Flow | 9.5 - 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.5 - 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 32.4 | 32.4 | ISO 868 |
| Tensile Strength at Break | 17.4 MPa | 2520 psi | 50 microns film; ASTM D882 |
| Tensile Strength, Yield | 4.20 MPa | 609 psi | 50 microns film; ASTM D882 |
| Elongation at Break | 650 % | 650 % | 50 microns film; ASTM D882 |
| Modulus of Elasticity | 0.0443 GPa | 6.43 ksi | ISO R527 |
| Dart Drop Test | 180 g | 0.397 lb | 50 microns film |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 90.0 °C | 194 °F | D.S.C. method |
| Vicat Softening Point | 62.0 °C | 144 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.2 % | 5.2 % | 50 micron film; ASTM D1003 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S70N Silicone Rubber
- PolyOne Geon™ Vinyl Flexible 90250 Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil LL 6235.19 Injection Molding Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 80/CF/12/TF/10/GY Polyacetal-copolymer, with carbon fiber and PTFE
- Wellman Wellamid® MRGF3822-BK 38% Mineral/10% Glass Fiber Reinforced Nylon 66, Heat Stabilized
- Total PPH 3727WZ Polypropylene, Injection Molding Grade
- Chevron Phillips K-Resin® XK41 Styrene-Butadiene Copolymer, Sheet Grade
- Eurotec® Tecopet® PT74 GR20 BK002 DA PET, 20% glass fiber reinforced, high heat stabilized, black
- Arlon 55276R026 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved