- Polymer Property : Tensile Strength at Break = 13.0 MPa
Polymer Property : Tensile Strength at Break = 13.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Konduit MT00EL PP LNP* Konduit* MT00EL is a Polypropylene base resin with thermal fillers. Characteristics of this grade are Thermal Conductivity and it is Low Extraactible.This data was supplied by SABIC-IP for th.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| DuPont Elvaloy® 1214 AC Ethylene and 14% Methyl Acrylate Copolymer
(discontinued **) Elvaloy® 1214 AC is intended for film coextrusion and injection molding. It can be recommended in film applications where softness, flexibility and excellent sealing properties are needed.Elvaloy®.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCD883 PPE-TPE Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 502.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCP781 PPE-TPE Flexible PPE-TPE injection grade. Low specific gravity with very good halogen free flame retardant performance. Suitable for over-molding applications such as plugs, strain relief's, and connecto.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCP781 PPE-TPE (Asia Pacific) Flexible PPE-TPE injection grade. Low specific gravity with very good halogen free flame retardant performance. Suitable for over-molding applications such as plugs, strain relief's, and connecto.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCP781 PPE-TPE (Europe-Africa-Middle East) Flexible PPE-TPE injection grade. Low specific gravity with very good halogen free flame retardant performance. Suitable for over-molding applications such as plugs, strain relief's, and connecto.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Solvay Specialty Polymers Cogegum® GFR/340 Polyolefin Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450C PU LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450C PUR (Asia Pacific) LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON FX98500 PE (Asia Pacific) LNP* Stat-kon* FX98500 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP 9H1100C LNP* Thermocomp* 9H1100C is a High Specific Gravity compound containing proprietary fillers. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| DuPont Elvaloy® 1913 AC Ethylene and 13% Methyl Acrylate Copolymer Elvaloy® 1913 AC is intended for film coextrusion and injection molding. It can be recommended in film applications where softness, flexibility and excellent sealing properties are needed.Elvaloy®.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| ELASTO UK Dryflex® 600850S SEBS Based Material, Filled Qualities, 85A Hardness, Natural The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material .. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| ELASTO UK Dryflex® 602900S SEBS Based Material, Filled Qualities, 90A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material .. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO 527-2/50 |
| ExxonMobil Exxtral™ BNT 010 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive exterior painted parts such as bumper fascia.Availability: Africa & Middle East, Asia Pacific, Europe, South A.. |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds CKL 009 Flexible PVC, Sheathing Lead Free General purposes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds CL 71 Flexible PVC, Sheathing General purposes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds CL 75/1 Flexible PVC, Sheathing General purposes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds GA 77/1 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds GA 89/3 Flexible PVC, Flame Retardant Sheathing Sheathing low emission acid fumes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds GK 83 Flexible PVC, Flame Retardant Sheathing Lead Free General purposes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds CKL 010 Flexible PVC, Sheathing Lead Free General purposes |
|||
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ISO R 527 |
| Fainplast Compounds HG 82 Flexible PVC, Sheathing for High Temperatures Sheathing general purposes |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
| Fainplast Compounds PG 56/B Flexible PVC, Extrusion Modified with Rubber Hydrocarbon resisting tubes |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Arkema Group LOTRYL® 18 MA 02 Copolymer Ethylene - Methyl Acrylate LOTRYL® 18 MA 02 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the methyl acrylate content, LOTRYL® 18 MA 02 is a polymer of .. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Braskem EB 861 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Coextruded films; Shrink films for pallets; general purpose; mulching films. Information p.. |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
| Fainplast Compounds PH 62 Flexible PVC, Transparent Extrusion Transparent profiles |
|||
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO R 527 |
| Fainplast Compounds PM 8220 Flexible PVC, Lead Free Various profiles |
|||