Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Oxford Polymers PPS-30GF-10PTFE-BK PPS, 30% Glass Fiber Reinforced, 10% PTFE Product Description: Glass Fiber (30% Reinforced), 10% PTFE, Polyphenylene sulfide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAppearance: BlackInformation pr.. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Polymer Resources NY66-IM1-G33-[color]-H Nylon 66, 33% Glass Reinforced, Toughened and Heat Stabilized Nylon 66, 33% Glass Reinforced, Toughened, Lubricated, and Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, tes.. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1033THL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Polymer Resources NY66-IM1-G33 Nylon 66, 33% Glass Reinforced, Toughened Nylon 66, 33% Glass Reinforced, Toughened and LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon g.. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1033TL Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES LNP LUBRICOMP* JFL36 is a compound based on Polyethersulfone resin containing 30% Glass Fiber, 15% PTFE. Added featurs of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON AE006 ABS LNP* STAT-KON* AE006 is a compound based on ABS containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF008 PBT (Asia Pacific) LNP* THERMOCOMP* WF008 is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem ATX152R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF004S PA 6 LNP* THERMOCOMP* PF004S is a compound based on Nylon 6 resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF004S PA 6 (Asia Pacific) LNP* Thermocomp* PF004S is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 LNP THERMOCOMP* PF006U is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of thie grade are: UV Stabilized. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF008 PBT LNP THERMOCOMP* WF008 is a compound based on PBT resin containing 40% Glass Fiber. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Chase Plastics CP Pryme® AC125G Acetal Copolymer, 25% Glass Fiber Reinforced Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Chase Plastics CP Pryme® PC130GR Polycarbonate, 30% Glass Fiber Reinforced, Mold Release Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
Chase Plastics CP Pryme® PC130R Polycarbonate, 30% Glass Fiber Reinforced Features: Good mold releaseForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | >= 128 MPa | >= 18600 psi | ASTM D4894 |
Adamas Adalon® 466 PTFE, Mineral/Organic Filler Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | ISO 527 |
BASF Ultramid® B3GM35 BK 60564 40% Glass/Mineral Filled PA6 (Dry) Description: Ultramid B3GM35 BK60564 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.Applications: industrial articles requiring medium rigidity and.. |
|||
Tensile Strength at Break | 128 MPa | 18600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RCL42 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. |