Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 100 MPa | 14500 psi | dry; ISO 527-1 |
Murtfeldt Murylon® A GF Nylon 66, Glass Reinforced Murylon® A’s impressive characteristics are enhanced with admixed glass fibers. This results in a clear improvement in cold flow behavior and dimensional stability, enabling higher static pressure.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ PS-30GF/2S Natural Polybutylene Terephthalate (PBT) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Tensile Strength at Break | <= 100 MPa | <= 14500 psi | ISO/R527 |
Polykemi AB SCANTEC PC S60R GF30 Polycarbonate, Glass-Fiber Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015HF PC (Asia Pacific) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only. UL94 V0 1.5 mm for BLACK; V1 1.5 mm for OTHER Color. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL34XXP PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL-4034 HP is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
DSM Akulon® K224-HG5 Nylon 6-25% Glass Reinforced (European and Asian Grade) (Cond)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | cond.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 30 H2.0 EF 000000 Nylon 6, Glass Fiber Reinforced PA 6, 30% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® DP 2131/20 W1 901317 Nylon 6, 20% Glass Fiber PA 6, injection molding grade, 20% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 20 H2.0, weather resistance, good heat-ageing resistance |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 20% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 218 V20 is used in all sectors of industry.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218C V10 PA66, 10% glass fiber, DRY Description: TECHNYL® A 218C V10 is a polyamide 66, reinforced with 10% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: Due to specially.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 50mm/min; ISO 527 |
Teijin Panlite® G-3430H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 30 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN3 PPE+HIPS (Europe-Africa-Middle East) Noryl GFN3 is a standard 30 % glass filled material with a HDT/A of 145C according to ISO 75 |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 MT15 V 25 Black 21N PA66, 25/15% glass/mineral fiber, Conditioned Description: Polyamide 66, reinforced with 25% of glass fiber and 15% of mineral filler, heat stabilized, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® A 218 MT15.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-93 |
Wellman Wellamid® MRGF25/15 22H-NBK1 40% Mineral/Glass Reinforced Nylon 66 Description: Mineral/Glass Reinforced Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-93 |
Wellman Wellamid® MRGF25/15 22H-NBK1/WE-1364 40% Mineral/Glass Reinforced Nylon 66 Description: Mineral/Glass Reinforced Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
Toyobo VYLOPET® EMC310TU Injection Molding Polyester Resin, Warpageless, High cycles Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesWarpagelessInformation provided by Toyobo. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GV 25 HWCP 25% Glass Fiber Nylon 6, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GV 25 HWUVCP 25% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
DSM Stanyl® TS250F4D Nylon 46-40% Glass Reinforced (Asian Grade) (Cond) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® HR5315HFS NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**) 15% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate with Improved Processing Crastin HR5315HFS is a 15% glass fiber reinforced moderatley toughened hydrolysis resistant polybutylene.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
Eurotec® Tecodur® PB70 GR30 NL XA60 PBT, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus, heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
Eurotec® Tecomid® NA40 AR20 NL HS PA6.6, 20% aramid fiber reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature
performance and .. |
|||
Tensile Strength at Break | 100 MPa @Temperature -40.0 °C |
14500 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |