Polymer Property : Flexural Yield Strength = 8700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	60.0 MPa @Strain 3.50 %	8700 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified PA 6-Copolymer, 15% glass fibers, injection molding impact modifiedInformation provided by LANXESS.
Flexural Yield Strength	60.0 MPa @Strain 3.50 %	8700 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BM 240 000000 Nylon 6, Mineral Reinforced PA 6, injection molding, 40% mineral, isotopic properties, low warpageInformation provided by LANXESS.
Flexural Yield Strength	60.0 MPa @Strain 3.50 %	8700 psi @Strain 3.50 %	Conditioned; ISO 178
Lanxess DurethanÂ® BM 240 H3.0 000000 Nylon 6, 40% Mineral PA 6, 40% mineral, injection molding, heat-ageing stabilized, low tendency to warp, isotopic properties
Flexural Yield Strength	60.0 MPa @Strain 3.50 %	8700 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® TP 142-011 900116 Nylon 6 PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Yield Strength	60.0 MPa @Temperature 232 °C	8700 psi @Temperature 450 °F	Autoclave Cured; [90°]16
Hexcel® HexPly® F652 Bismaleimide Resin, Carbon Tape Form Material Description: T6T145; Fiber: T300-6KInformation provided by HexCel