Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 80.0 MPa | 11600 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Akulon® PA6 G.Oil - Omniamid Oil - at 50% RH Cast Nylon 6 with the addition of 6% of special lubricating oil which remains in solution in the material. The unique method of production results in a micro distribution of oil particles with a hom.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Omniamid PA 6 - Akulon 6 - at 50% RH Semi-crystalline polymer of polyamide obtained by the polymerisation of the caprolactam. Its large popularity is due to both its good overall features as well as its cost-performance relationship. T.. |
|||
Ball Indentation Hardness | 80.0 - 270 MPa | 11600 - 39200 psi | Average value: 180 MPa Grade Count:22 |
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl.. |
|||
Ball Indentation Hardness | 80.0 - 160 MPa | 11600 - 23200 psi | Average value: 114 MPa Grade Count:10 |
Overview of materials for Nylon 66, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Impact Grade". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | ISO 2039 |
GEHR Plastics PVDF Polyvinylidene Fluoride Polyvinylidene fluoride shows a higher tensile strength, pressure resistance and dimensional stability than the related PTFE, but friction and insulation properties are lower. PVDF has a high mechan.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | ISO 2039-1 |
Styrolution Luran® S 767KE ASA Luran S 767KE is particular suitable for co-extrusion with PVC at low temperature. Hereby, it provides a glossy surface finish.Enhanced flowabilitySuitable for co-extrusion with PVCEnables high glos.. |
|||
Ball Indentation Hardness | 80.0 MPa @Load 36.5 kg, Time 30.0 sec |
11600 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Styrolution Luran® S 777 K UV Black 56625 ASA Description: Easy flowing injection molding grade with good toughness and heat distortion resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | ISO 2039-1 |
Styrolution Terluran® HI-12 ABS Terluran HI-12 is an injection molding grade of ABS with a very high toughness and easy flow.Very high toughnessEasy flowingUL 94 HB (1.6 & 3.2 mm)Information provided by Styrolution |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® 1S XE 4224 nat PA1010 Product Description: Grilamid XE 4224 natural is a heat and UV stabilized high viscosity polyamide 1010 (PA1010), designed for extrusion. In addition the product can be used for thicker injection mo.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BG-15 PA6-GF15 Product description: Grilon BG-15 is a heat stabilized PA 6 injection molding grade with 15% glass fiber reinforcement. Grilon BG-15 has the following important properties: Good surface finishGood b.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BG-15 S PA6-GF15 Product description: Grilon BG-15 S is a heat stabilized PA6 injection molding grade with 15% glass fibers. Grilon BG-15 S has the following important properties: Excellent surface finishEasy flowin.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BG-15/2 PA6-GF15 Product description: Grilon BG-15/2 is a heat stabilized PA6 injection molding grade with 15% glass fibers. Grilon BG-15/2 has the following important properties: Good surface finishEasy processingG.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BG-30 EC PA6-GF30 Information provided by EMS Grivory |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BT 40 Z PA6 Product description: Grilon BT 40 Z is an unreinforced, normal viscosity, impact modified polyamide blend with amorphous and semi-crystalline components. Grilon BT 40 Z has the following important p.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® LM-05 HX nat PA12 Product description: Grilamid LM-05 HX natural is a medium viscosity, heat-stabilized nanocomposite PA12 extrusion and injection molding grade. The special features of Grilamid LM-05 HX natural are:.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® TSGK-30/4 X PA666-(GF+GB)30 Product description: Grilon TSGK-30 X/4 is a heat stabilized PA 66 + PA 6 injection molding grade with a 30% reinforcement combination (glass fibers and glass beads). Grilon TSGK-30/4 X has the foll.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® TSS/2 FA PA666 Product description: Grilon TSS/2 FA is an unreinforced, heat stabilized, normal viscosity PA66 + PA6 injection molding grade. Grilon TSS/2 FA has the following important properties: Excellent flow .. |
|||
Ball Indentation Hardness | 80.0 MPa @Time 30.0 sec |
11600 psi @Time 0.00833 hour |
DIN 53 456 |
Hippe PP Polypropylene Lower density compared with PE. Higher hardness and stiffness and better reset features. Non-fragile. Toughness in cold lesser than that of PE. Higher working temperatures than PE, not aromatic-.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® TR 90 NZZ nat PAMACM12-I Product description: Grilamid TR 90 NZZ natural is an amorphousthermoplastic polyamide, based on aliphatic and cycloaliphatic units. Grilamid TR 90 NZZ natural offers a variety of interesting proper.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | H358/30; ISO 2039-1 |
Chi Mei Polylac® PA-763 ABS - Flame Retardant F.R. High Heat Weather Resistant |
|||
Ball Indentation Hardness | 80.0 MPa @Load 36.5 kg, Time 30.0 sec |
11600 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
BASF Ultraform® N2650 Z4 (LEV) POM Description: Is a POM + PUR, elastomer-modified injection-molding grades with high impact strength for clips, snap and fastening elements, also for components subject to impact stress.Information pr.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | H358/30; ISO 2039-1 |
Chi Mei Polylac® PA-763A ABS - Flame Retardant F.R. High Heat |
|||
Ball Indentation Hardness | 80.0 - 120 MPa | 11600 - 17400 psi | Average value: 99.3 MPa Grade Count:26 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Molded". Each property range of values reported is minimum and ma.. |
|||
Ball Indentation Hardness | 80.0 MPa | 11600 psi | Fm=358N; Ø 50x4mm; ISO 2039-1 |
SYNTHOS Krasten® 336M High Impact Polystyrene Easy flow grade. Processed by injection moulding of intricate and thin-walled products that enables high production output.Synthos was formerly known as Kaucuk. All information provided by Synthos. |