Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 45.0 MPa | 6530 psi | |
Plastcom SLOVALEN PC 71 T 20 PP, 20% mineral filling FeaturesModified copolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrin.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | |
Plastcom SLOVALEN PH 32 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | |
Plastcom SLOVALEN PH 99 GB 30 LS PP, 30% glass beads, mod. of mech. properties FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass beads, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
Flexural Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
Polimeri Europa Edistir R 321P Polystyrene Medium impact polystyrene combining easy flow and high stiffness. For injection moulding of parts with low thickness and high rigidity. Designation: Thermoplastics ISO 2897-PS-I,M,083-12-04-30Applic.. |
|||
Flexural Strength | 45.0 - 60.0 MPa | 6530 - 8700 psi | ASTM D790-03 |
Proto3000 Objet Digital Materials™ DM_8425 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide.. |
|||
Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
Polykemi AB POLYfill PPHC K2040H Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
Polykemi AB POLYfill PPHC TS25020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 45.0 MPa | 6530 psi | |
Reliance Industries Polypropylene - Suzorite mica (untreated) filler Information provided by Reliance Industries |
|||
Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
Polykemi AB POLYfill PPC T10030 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
Polykemi AB POLYfill PPH BK901010 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 45.0 MPa | 6530 psi | 0.1 in/min; ASTM D790 |
Ineos Nova 8077 High Performance Styrenic Enhanced Polystyrene
(discontinued **) High flow, Special additives can be incorporate to improve properties such as coefficient of friction and static dissipation, Custom colorsApplications: Injection molding, Designed for thin wall app.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
Nilit FRIANYL C73 MG40 Nylon 6.6/6 for injection molding, 40% mineral filled Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 45.0 MPa @Temperature 1500 °C |
6530 psi @Temperature 2730 °F |
|
MarkeTech MC-LD and MC-MD Ultra High Temperature Machinable Ceramics For very high temperatures or where thermal conductivity or thermal shock is important, these machinable alkaline/alkaline earth zirconium phosphate ceramics (NaZr2P3O12 or BaZr4P6O24) are recommend.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Ineos Nova Zyntar® 7000 Flame Retardant Polystyrene Features:General purpose workhorse resinGood flow for injection moldingUL94 V-0 @ 1.5 mm for all colors UL94 5VA rating FOAMED @ 4.6 mm, 0.87-1.07 g/cc density, natural colorCustom colors availableA.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
Ineos ABS Triax® 1185 ABS/Nylon Alloy, Injection Molding Grade Triax® 1185 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with excellent processability, good chemical resistance, g.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | |
SPS Guang Zhou FILLMAâ„¢ 5002F30C Mineral Filled Polypropylene Characteristic: 30%wt of Sulfate Calcium filled, low odor, good glossApplications: Household appliance parts, office suppliesInformation Provided by SPS (Guang Zhou) Ltd. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Teknor Apex Sinpolene CPP1050 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 40% Filler by Weight Features: Homopolymer Uses: Appliance Components; Furniture; Housings F.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | GB/9341 |
Zhejiang Juner JEPPB003 High Glossy PP Applications: Electric Rice CookerInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene DescriptionPolyflam® RPP 1360 is a UL 94 V0 rated, non-halogenated homopolymer polypropylene flame retardant compound. Information provided by A. Schulman. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Polyram RamOfin PPH106 Polypropylene, Injection Molding polypropylene with molybdenum for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
Eurostar Starpylen MFM43S PP, Glass/Mineral Filled, Injection Molded Starpylen MFM43S is a Mineral Filled, Glass Fiber Reinforced, Polypropylene Injection Molding Resin, also recognized as Starpylen WV 30VMC S37/7 Black 301Information provided by Eurostar. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0334T30L Talc Reinforced |
|||
Flexural Strength | 45.0 MPa | 6530 psi | STN EN ISO 178 |
Plastcom SLOVALEN PH 51 T 15 Polypropylene Homopolymer, 15% Mineral Filled FeaturesModified homopolymer PP for injection moulding with the content of 15% mineral filler. Increased rigidity, strength and thermal use up to 130°C. Decreased shrinkage. General application .. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | |
Plastcom SLOVALEN PH 73 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
Polykemi AB POLYfill PPHC K8030 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
Borealis MB350WG Polypropylene Compound, Mineral Filled MB350WG is a 30% mineral filled polypropylene compound intended for injection molding. This material has a very high impact strength while maintaining good stiffness and is easy to process. Applic.. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Polyram RamOfin PPC359T4 Polypropylene, 20% Mineral Filled 20% mineral filled, heat stabilized and impact modified for polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Teknor Apex Sinpolene CPP1040 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 40% Filler by Weight Features: Homopolymer Uses: Appliance Components; Furniture; Housings F.. |