Polymer Property : Flexural Strength = 31900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 220 MPa	<= 31900 psi	ISO 178
Polykemi AB SCANMID 6 B12^ F25 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB
Flexural Strength	220 MPa	31900 psi	ISO 178
Nilit FRIANYL B63 HH-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced Nylon 6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	220 MPa	31900 psi
Lehmann & Voss LUVOCOMÂ® 19-7816 Polyamide 46, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Electrical..
Flexural Strength	220 MPa	31900 psi	ISO 178
Grupo Repol DinalonÂ® A1S25 G25 PA66 25% Glass Fiber Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Strength	220 MPa	31900 psi
Lehmann & Voss LUVOCOMÂ® 1-7817 Polyamide 66, with carbon fiber, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Electrical..
Flexural Strength	220 MPa	31900 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2310F PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Strength	220 MPa	31900 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2310R PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength	220 MPa	31900 psi	ISO 178
Solvay Specialty Polymers RytonÂ® R-4 Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4 and R-4-02 40% glass fiber reinforced polyphenylene sulfide compounds provide a good combination of mechanical and electrical properties with outstanding chemical resistance, even at e..
Flexural Strength	220 MPa	31900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC (Asia Pacific) LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Flexural Strength	220 MPa	31900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF006L PA 66 (Asia Pacific) LNP* Thermocomp* RF006L is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible.
Flexural Strength	220 MPa	31900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 LNP* THERMOCOMP* RF006LXP is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible.
Flexural Strength	220 MPa	31900 psi	ISO 178
Solvay TECHNYLÂ® C 246SI V30 PA6, 30% glass filled, DRY Description: Polyamide 6, reinforced with 30 % of glass fiber, with high impact resistance, for injection molding.Available in: Asia Pacific , Europe and North AmericaProduct Applications: Having go..
Flexural Strength	220 MPa	31900 psi	ASTM D790
SABIC Innovative Plastics LNP VERTON RV008E PA 66 LNP* VERTON* RV008E is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.
Flexural Strength	220 MPa	31900 psi	ISO 178
Polyram PlusTek PA840G7 Nylon 6.6 for Injection Molding, 35% Glass Fibers Reinforced, Impact Modified 35% Glass fiber reinforced, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
Flexural Strength	220 MPa	31900 psi	ASTM D790
Polyram PlusTek PB300G5 Nylon 6, 15% Glass Fiber 15% glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	220 MPa	31900 psi	ASTM D790
Toyobo VYLOPET® EMC132-02 Injection Molding Polyester Resin, Flame Resistant Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo.
Flexural Strength	220 MPa	31900 psi	ISO 178
Polyram RamTough PZ307G6 Polycarbonate, 30% Glass Fiber, UV Stabilized 30% glass fiber reinforced polycarbonate, UV stabilized, for injection molding applications.Information provided by Polyram.
Flexural Strength	220 MPa	31900 psi	Rigidty. Elastic bending fatigue, Transverse
CLAL-MSX NICLAFOR® 1000 TB Quenched Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Flexural Strength	220 MPa	31900 psi	ISO 178
Eurotec® Tecomid® NA40 GR25 NL XA 42 PA 6.6 25% glass fiber reinforced, UL94 V0, red phosphorus Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Flexural Strength	220 MPa	31900 psi	ASTM D790, ISO 178
EPICHEM PA 6 GF 30 Polyamide 6, 30% Glass Characteristics: medium viscosity, 30% glass fibre filled
Flexural Strength	220 MPa @Temperature 65.0 °C	31900 psi @Temperature 149 °F	ASTM Test
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry) Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio..
Flexural Strength	220 MPa	31900 psi	ASTM D790
Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled Standard V-0 Grade. Delivers increased fluidity and weld strength. Well suited for a wide range of electrical and electronic components.
Flexural Strength	220 MPa	31900 psi	at max force; ISO 178
BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el..