- Polyram RamTough PZ307G6 Polycarbonate, 30% Glass Fiber, UV Stabilized
Polyram RamTough PZ307G6 Polycarbonate, 30% Glass Fiber, UV Stabilized
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough PZ307G6 Polycarbonate, 30% Glass Fiber, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced polycarbonate, UV stabilized, for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ISO 2577 |
| Melt Flow | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Quadrant EPP Ertacetal® H-TF POM-H, PTFE-filled, extruded (ISO Data)
- Chevron Phillips Marlex® 1409 Injection Molding Resin (discontinued **)
- Karina 67/200-D-IS-SD Clear PVC Compound
- Techmer ES Elastoblend® PA6 GF43 IM L BKN 43% Glass Filled
- Techmer ES HiFill® PA6 GF30 HF L BK 30% Glass Filled
- Teknor Apex Monprene® MP 1869 Thermoplastic Elastomer
- Lubrizol Isoplast® 301 Engineering Thermoplastic Polyurethane Resin
- Asahi Glass Lumiflon LF-302 Solvent Soluble Fluoropolymer w/ isocyanate hardening agent
- Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved