Polymer Property : Flexural Strength = 49.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 49.0 MPa	<= 7110 psi	ISO 178
Polykemi AB POLYfill PPC T12020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 49.0 MPa	<= 7110 psi	ISO 178
Polykemi AB POLYfill PPC T16020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	49.0 MPa	7110 psi	3.5%; ISO 178
GEHR Plastics ECTFE Polyethylene Chlorotrifluoroethylene Ethylene-Chlortrifluorethylene exhibits an extraordinary impact strength at temperatures ranging from -76Â°C to 150Â°C. A great part of the product properties attributes to the very smooth surfa..
Flexural Strength	49.0 MPa	7100 psi	ASTM D790
Techmer ES HiFillÂ® PA6 0500 Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforFeatures: High Specific GravityProcessing Method: Injection MoldingInformation provided by TP Composites, Inc..
Flexural Strength	49.0 MPa	7110 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Europe-Africa-Middle East) LNP* Stat-Loy* A30009 is a compound based on Acrylonitrile Butadiene resin, containing Proprietary Filler, Flame Retardant. Added features include : Permanent Antistatic, Flame retardant.
Flexural Strength	49.0 MPa	7110 psi	ISO 178
SABIC Innovative Plastics LNP STAT-LOY A3000TXB ABS LNP* STAT-LOY* A3000TXB is a compound based on ABS resin. Added features of this material include: Antistatic, Transparent, Formulated with FDA Food Contact Additives and Bioassessed to ISO 10993...
Flexural Strength	49.0 MPa	7110 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® GC-0770 H ABS/PET, Unreinforced Recycled Eco-friendly Post-Consumer recycled PET.Information provided by Samsung Cheil Industries.
Flexural Strength	49.0 MPa	7110 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® NT-7310 ABS, Unreinforced FR Flame-retardant ABS that can be used in printer frames etc.Information provided by Samsung Cheil Industries.
Flexural Strength	49.0 MPa	7110 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-LOY K3000Z Acetal LNP* STAT-LOY* K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat.
Flexural Strength	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	ASTM D790
Supreme Petrochem SH 2114 High Impact Polystyrene Characteristics Very high impact strength Easy processing High heat Processing Extrusion MoldingApplications Toys, shoe heels, cosmetic boxes, pill vials Luggage cases Blending with clear polys..
Flexural Strength	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	ASTM D790
Supreme Petrochem SP 265 Toughened Polystyrene CharacteristicsGood clarity High dart impact strength High heat resistance Good stiffnessProcessing Extrusion Vacuum forming Applications Disposable glasses & bowls Deep draw formed products Ther..
Flexural Strength	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	ASTM D790
Supreme Petrochem SP6433 9710 Medium Impact Polystyrene Characteristics High flow Good toughness Good shine Available in various colors Processing Injection molding Extrusion Applications Pipes & profiles for wiring Beading for furniture and tables ..
Flexural Strength	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	ASTM D790
Supreme Petrochem SP6489 9940 High Impact Polystyrene Characteristics High flow Good toughness Available in black only Processing Injection moldingApplications TV and audio-video back and front cover Material Status: Commercial : ActiveAgency Ratings..
Flexural Strength	49.0 MPa	7110 psi	ASTM D790
SABIC Innovative Plastics NORYL PX2795 PPE+HIPS (Asia Pacific) PPE/HIPS, unfilled, FR-V1, 85 oC
Flexural Strength	49.0 MPa	7110 psi	ISO 178
Unitika A1030JR PA6, Conditioned Information provided by Unitika Ltd.
Flexural Strength	49.0 MPa	7100 psi	8 lb Core, 6 hrs @ 220°F, Vacuum Bag
Zyvex Performance Materials Aroply™ 250 Nano-Engineered Composite Film Adhesive Aroply™ 250 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported knitted nylon carrier. Cured adhe..
Flexural Strength	49.0 MPa	7100 psi	ASTM D638
Plastics Group Polifil® GFRMPPCC-10 10% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap..
Flexural Strength	49.0 MPa	7100 psi	ASTM D790
Ecomass® 1050ZD96 Tungsten Powder Filled Polyamide Alloy, Injection Molding Grade High Specific Gravity, Tungsten Powder Filled Polyamide (PA) Alloy, Good Toughness, Product Form - PelletsProcessing Method: Injection MoldingNontoxic alternative to Lead, weighting, balancing and ..
Flexural Strength	49.0 MPa	7100 psi	ASTM D790
Ecomass® 1080ZB92 Filled Polyamide Nontoxic alternative to Lead (Pb), radiation shielding applications.Moderate Specific GravityFilled Polyamide (PA) alloyExcellent ToughnessInformation provided by Technical Polymers
Flexural Strength	49.0 MPa	7100 psi	ASTM D790
Ecomass® 1080ZD95 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications.High Specific GravityTungsten Powder Filled Polyamide (PA) AlloyExcellent ToughnessInformation provided b..
Flexural Strength	49.0 MPa	7110 psi	ASTM D790
Entec Hypro™ PPC-GF10 Natural Impact Polypropylene, 10% Glass Reinforced Information provided by Entec
Flexural Strength	49.0 MPa	7110 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336T30L1 Talc Reinforced
Flexural Strength	49.0 MPa	7110 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 152 Polypropylene, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	49.0 MPa	7100 psi
3M Scotchkote™ RG 501 Urethane Metal Repair Scotchkote Urethane Metal Repair RG 501 has been specifically developed as a rapid curing repair system for rebuilding and repairing equipment requiring good mechanical strength.Product Features:Com..
Flexural Strength	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	ASTM D790
Supreme Petrochem SP6409 High Gloss Polystyrene Characteristics High gloss in co-extrusion Improved dart impact strength of co-extruded sheets Processing Co-extrusion cap layer Applications Gloss cap layer for refrigerator liner and other formin..
Flexural Strength	49.0 MPa	7110 psi	0.5 in/min; ASTM D790
Ineos Nova Zylar® 94-580-A High Performance Styrenic, Acrylic Copolymer (discontinued **) Excellent heat distortion temperature, High clarity, strength and toughness, Enhanced mold releaseApplications: Industrial covers and housings, Paper towel dispenser covers, Appliance partsInjection..