- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Samsung Cheil Industries Starex® NT-7310 ABS, Unreinforced FR
Samsung Cheil Industries Starex® NT-7310 ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® NT-7310 ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame-retardant ABS that can be used in printer frames etc.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 6.35 mm |
2.39 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.57 J/cm @Thickness 3.17 mm |
2.94 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 6.40 mm |
176 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 1.50 - 3.00 mm |
V-0 @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 500 PC (Asia Pacific)
- Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a
- Premix Thermoplastics PRE-ELEC® 12-031 (discontinued **)
- Lanxess Durethan® BKV 50 H2.0 901510 Nylon 6, 50% Glass Fiber
- Techmer ES HiFill® PA6 GF20 L 20% Glass Filled
- SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA (Asia Pacific)
- DuPont™ Kapton® 50HN Polyimide Film, 13 Micron Thickness
- DuPont Performance Polymers Zytel® PLS FR95G15DH2 BK269 Nylon 6
- DuPont Teijin Films Melinex® 3380 & CORE 1 Polyester Film
- Austin Novel Materials Texalan® 482A Polyester-based TPU
Copyright © lookpolymers.com All Rights Reserved