Unitika A1030JR PA6, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	Unitika
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika A1030JR PA6, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Water Absorption	1.8 % @Time 86400 sec	1.8 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.8 %	2.8 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Thickness 3.20 mm	0.0090 in/in @Thickness 0.126 in
Linear Mold Shrinkage, Transverse	0.011 cm/cm @Thickness 3.20 mm	0.011 in/in @Thickness 0.126 in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	85	85	ISO 2039
Tensile Strength, Yield	55.0 MPa	7980 psi	ISO 527-1/-2
Elongation at Break	150 %	150 %	ISO 527-1/-2
Elongation at Yield	22 %	22 %	ISO 527-1/-2
Tensile Modulus	1.20 GPa	174 ksi	ISO 527-1/-2
Flexural Strength	49.0 MPa	7110 psi	ISO 178
Flexural Modulus	1.20 GPa	174 ksi	ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179-1
Charpy Impact, Notched	3.10 J/cm²	14.8 ft-lb/in²	ISO 179-1

Thermal Properties	Metric	English	Comments
CTE, linear	96.0 µm/m-°C	53.3 µin/in-°F	ISO 11359-2
Flammability, UL94	V-2 @Thickness 0.840 mm	V-2 @Thickness 0.0331 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	8.00e+11 ohm-cm	8.00e+11 ohm-cm	IEC 60093
Dielectric Constant	3.7 @Frequency 1.00e+6 Hz	3.7 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	33.0 kV/mm @Thickness 1.00 mm	838 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.080 @Frequency 1.00e+6 Hz	0.080 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	>= 600 V	>= 600 V	IEC 60112