Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | <= 34.0 MPa | <= 4930 psi | ISO 178 |
Polykemi AB POLYfill PP CQX15015 R3 UV Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ISO 178 |
Nilit FRIANYL B63 CU90 Nylon 6.6 for injection molding, 90% copper filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS (Asia Pacific) LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing PTFE. Added features of this material include: Internally Lubricated, High Impact. |
|||
Flexural Strength | <= 34.0 MPa | <= 4930 psi | ISO 178 |
Polykemi AB POLYfill PP EIP16020 F PP Mineral Reinforced, Extrusion Grade, Low CLTE Information provided by Polykemi AB |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 0.1 in/min; ASTM D790 |
Ineos Nova 765 High Performance Styrenic Enhanced Polystyrene
(discontinued **) High flow, High impact, Color stable, Custom colorsApplications: High flow, multi-purpose injection molding grade where color stability is a requirement, Toys, Appliance, Computer peripheralsPerform.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 0.1 in/min; ASTM D790 |
Ineos Nova 782 High Performance Styrenic Enhanced Polystyrene
(discontinued **) High flow, Custom colorsApplications: Multi-purpose injection molding where custom color is a requirement, Toys, Appliance, Computer peripheralsPerformance grades of polystyrene are engineered to ha.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 0.1 in/min; ASTM D790 |
Ineos Nova Zyntar® 7001 High Performance Flame Retardant Polystyrene
(discontinued **) Super high flow, Reduced processing temperatures, Reduced processing time, Improved aesthetics, Custom colorsApplications: Injection molding, Gas-assist injection molding, Hard to fill cavities, suc.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
Honeywell Aegis™ PL220HS High Viscosity, Heat Stabilized, Flexible Nylon 6
(discontinued **) Description: Aegis PL220HS is a high viscosity, heat stabilized, flexible nylon 6 especially suited to the production of large diameter extrusion or blow molding profiles offering a combination of g.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 2mm/min; ASTM D790 |
Kingfa FRHIPS-117 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6 & 3.2mmExcellent balance properties, high strengthExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingTV & Audio housingElectrica.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | |
Kuraray HYBRAR® PS3 Thermoplastic Rubber-Polystyrene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP (Asia Pacific) LNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized, Low Extractible. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY M3000 PP (Europe-Africa-Middle East) LNP* Stat-loy* M3000 is a compound based on Polypropylene resin. Added features of this material include: Antistat, High Impact. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS LNP THERMOCOMP* AH0230A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Europe-Africa-Middle East) LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ISO 178 |
Unitika A1030BRL PA6, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3727 is a 24% mineral filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3727 is a 24% mineral filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3727 is a 24% mineral filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ISO 178 |
Unitika A1030SR PA6, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3727 is a 24% mineral filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 1.0 in/min; 0.125" thickness; ASTM D-790 |
Chevron Phillips K-Resin® XK44 SBC K-Resin® Styrene-Butadiene Copolymer (SBC)Applications:Thermoformed clam shell packagingThermoformed blister packsThermoformed medical traysBlow molded productsFeatures:Good clarityGood stiffnessGo.. |
|||
Flexural Strength | 34.0 MPa @Strain 3.50 % |
4930 psi @Strain 3.50 % |
ISO 178 |
DuPont Performance Polymers Delrin® 100ST NC010 Acetal (POM)
(Unverified Data**) Super Toughened High Viscosity Acetal Homopolymer Delrin 100ST NC010 is a super tough high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed part.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PH-88S Polystyrene - Extrusion Extrusion |
|||
Flexural Strength | 34.0 MPa | 4930 psi | After conditioning at 23°C and 50% RH; ISO 178 |
Arkema Group Orgalloy® LE 60 HM Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
Aclo Accutech Polyethylene HD0232G20CV High Density Glass Reinforced Chemically Coupled Approved to GMP.PE.018 Black A12438 |
|||
Flexural Strength | 34.0 MPa @Temperature 120 °C |
4930 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ISO 178 |
Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded Vydyne® 66B and 66J are members of a family of unreinforced extrusion grade Nylon 66 resins. They are available in natural color. These resins offer high strength, rigidity, and toughness for a bro.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 102 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3727 is a 24% mineral filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing 5% PTFE. Added features of this material include: Internally Lubricated, High Impact. |