Arkema Group Orgalloy® LE 60 HM Polyamide Alloy

Category Polymer , Thermoplastic , Nylon
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® LE 60 HM Polyamide Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO R1183
Water Absorption 0.80 %
0.80 %
23°C / 24 hrs; ISO 62
Moisture Absorption at Equilibrium 1.8 %
1.8 %
23°C / 50% RH; ISO 62
6.4 %
6.4 %
in 23°C water; ISO 62
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 235 °C
 0.90 g/10 min

@Load 4.76 lb,
Temperature 455 °F
 after drying; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 54.0 MPa
7830 psi
ISO R527
Tensile Strength, Yield 39.0 MPa
5660 psi
ISO R527
Elongation at Break 330 %
330 %
ISO R527
Elongation at Yield 5.0 %
5.0 %
ISO R527
Modulus of Elasticity 1.55 GPa
225 ksi
ISO R527
Flexural Strength 34.0 MPa
4930 psi
After conditioning at 23°C and 50% RH; ISO 178
Flexural Modulus 1.20 GPa
174 ksi
After conditioning at 23°C and 50% RH; ISO 178
Charpy Impact, Notched 2.80 J/cm²
13.3 ft-lb/in²
After conditioning at 23°C/50%RH; ISO 179/Af
20.0 J/cm²

@Temperature -20.0 °C
 95.2 ft-lb/in²

@Temperature -4.00 °F
 After conditioning at 23°C/50%RH; ISO 179/Af
Tensile Creep Modulus, 1 hour 1350 MPa
196000 psi
ISO 899-1
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO R1218
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
NFC 26 220