Unitika A1030SR PA6, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	Unitika
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika A1030SR PA6, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	1.8 % @Time 86400 sec	1.8 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.8 %	2.8 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.20 mm	0.010 in/in @Thickness 0.126 in
Linear Mold Shrinkage, Transverse	0.013 cm/cm @Thickness 3.20 mm	0.013 in/in @Thickness 0.126 in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	90	90	ISO 2039
Tensile Strength, Yield	38.0 MPa	5510 psi	ISO 527-1/-2
Elongation at Break	>= 200 %	>= 200 %	ISO 527-1/-2
Elongation at Yield	24 %	24 %	ISO 527-1/-2
Tensile Modulus	0.940 GPa	136 ksi	ISO 527-1/-2
Flexural Strength	34.0 MPa	4930 psi	ISO 178
Flexural Modulus	0.900 GPa	131 ksi	ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179-1
Charpy Impact, Notched	4.10 J/cm²	19.5 ft-lb/in²	ISO 179-1

Thermal Properties	Metric	English	Comments
CTE, linear	96.0 µm/m-°C	53.3 µin/in-°F	ISO 11359-2
Flammability, UL94	V-2 @Thickness 0.750 mm	V-2 @Thickness 0.0295 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	8.00e+11 ohm-cm	8.00e+11 ohm-cm	IEC 60093
Dielectric Constant	3.7 @Frequency 1.00e+6 Hz	3.7 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	33.0 kV/mm @Thickness 1.00 mm	838 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.080 @Frequency 1.00e+6 Hz	0.080 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	>= 600 V	>= 600 V	IEC 60112