Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Oxford Polymers 30CF 30% Carbon Fiber Reinforced Polyphenylene Sulfide 30% Carbon Fiber Reinforced Polyphenylene SulfideInformation provided by Oxford Polymers. |
|||
Flexural Strength | 228 MPa @Temperature 23.9 °C |
33000 psi @Temperature 75.0 °F |
Dry; 8HS form; ASTM D790 |
Park Electrochemical Nelcote® F-555 Phenolic Prepreg, NARC/CYDSA Reinforced Nelcote® F-555 is a carbon-filled MIL-R-9299 phenolic resin optimized for coating Carbonized Rayon cloth. F-555 is used extensively in the manufacture of high temperature rocket nozzles, heat shiel.. |
|||
Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
IDI Composites C-206 Thermoset Polyester, Sheet CORROSION - (Patent pending). Versatile family of compounds designed for pressurized and thermo-mechanically stressed applications. Excellent corrosion resistance and high strength.Data provided by .. |
|||
Flexural Strength | 228 MPa | 33100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP QFN16 PA 6/10 LNP* LUBRICOMP* QFN16 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 5% MOS2. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Techmer ES Electrablend® PPS 05002 Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementFeatures: Electrically ConductiveInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Techmer ES HiFill FR® PA6/6 GF30 FR NAT 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Lubricated and Heat StabilizedAppear.. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF30 HF L BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Lubricant Features: Lubricated and High FlowAppearance: BlackInformation provi.. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF40 L 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Lubricant Features: LubricatedInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Techmer ES HiFill® PEI GF30 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Techmer ES Plaslube® J-1/CF/15/TF/20 NAT PA66 |
|||
Flexural Strength | 228 MPa | 33100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP QFL36 PA 6/10 LNP LUBRICOMP* QFL36 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 228 MPa | 33100 psi | GB/T 9341-2008 |
Sichuan Deyang Haton® hMR61 Polyphenylene Sulfide, Glass & Mineral Reinforced Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF PX06417 PA 6 LNP THERMOTUF* PX06417 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
Westlake Plastics Tempalux® 30% GF Polyetherimide An amorphous thermoplastic polyetherimide, stock shapes from ULTEM® resin possess a combination of useful characteristics, including high strength at elevated temperatures, high modulus, and broad .. |
|||
Flexural Strength | 228 MPa @Temperature 22.8 °C |
33000 psi @Temperature 73.0 °F |
ASTM D790 |
Ensinger TECATOR™ TI 5013 Polyamide-imide (PAI) TECATOR™ is a high performance melt processable polyamideimide that maintains its excellent mechanical and wear properties in temperature environments exceeding 500°F. Stock shapes from Ensinger .. |
|||
Flexural Strength | 228 MPa | 33000 psi | 10 oz glass cloth laminate |
BCC Products BC 5114 Epoxy Laminating System BC 5114 is a gray low viscosity laminating system. This heat resistant resin exhibits excellent wet out, reasonable working time and may be used at room temperature without post-curing. For use abov.. |
|||
Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
PolyOne Lubri-Tech™ NI-30CF/10T-2S Nylon 6/10, Carbon Fiber Reinforced, PTFE/Silicone Lubricated
(discontinue Description/Features:Carbon Fiber ReinforcedPTFE/Silicone LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
Ashley Polymers Ashlene® PE126 PET Polyester, 30% Glass Reinforced PET Polyester, with 30% glass reinforcement.Data provided by the manufacturer |
|||
Flexural Strength | 228 MPa | 33100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Verton RV006ESV_GY7E071 PA 66 Preliminary Data for 30% long glass fiber, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region. |