- Polymer Property : Flexural Strength = 106 MPa
Polymer Property : Flexural Strength = 106 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Quantum Polysulfone Information provided by Quantum Advanced Engineering Plastics |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Polymer Resources NY6-GP1 General Purpose Nylon 6 General Purpose Nylon 6, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® P-3703 Polysulfone (PSU)
(Unverified Data**) Udel P-3703 is a high-flow grade of polysulfone intended for injection molding applications with thin walls or long flow lengths. This grade has higher flow than Udel P-1700 and a slightly greater t.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® P-1800 Polysulfone (PSU)
(discontinued **) Udel P-1800 is a powdered grade of polysulfone with molecular weight similar to that of Udel P-1700 polysulfone. It is well suited for the fabrication of porous membranes that can be made into hollo.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RAL22 is a compound based on PA66 resin containing PTFE, Aramid Fiber. Added Features: Internally Lubricated |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Solvay Specialty Polymers AvaSpire® AV-621 Polyaryletherketone (PAEK) AvaSpire® AV-621 is an unreinforced polyaryletherketone (PAEK) that offers improved ductility and impact strength relative to PEEK while retaining most of the key performance attributes of PEEK. .. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU) Udel® P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® P-1710 Polysulfone (PSU) Udel® P-1710 polysulfone (PSU) is a tough, rigid, high-strength thermoplastic that is suitable for continuous use up to 300°F (149°C). The resin is resistant to oxidation and hydrolysis and.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® P-3500 LCD MB Polysulfone (PSU) Udel® polysulfone is a tough, rigid, high-strength thermoplastic with outstanding hydrolytic resistance. Udel® P-3500 LCD MB series polymers are particularly well suited for the fabrication of.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON KEP33 Acetal (Asia Pacific) LNP STAT-KON* KEP33 is a compound based on Acetal resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP Cycoloy_C7210A PC+ABS LNP* Thermocomp* Cycoloy_C7210A isa a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. Very good modulus-ductility balance. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Styrolution Polystyrol 168 N GR 21 PS Description: Polystyrol 168 N is a high molecular, heat grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. As blend component with high impact.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MF004SU PP LNP* THERMOCOMP* MF004SU is a compound based on Polypropylene containing 20% Glass Fiber. Characteristics of this grade are: Heat Stabilized, Chemically Coupled, UV Stabilized. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Styrolution PS 168N GPPS Styrolution PS 168N is a high molecular weight, heat resistant grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. Also use as a blend componen.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® P-1700 Polysulfone (PSU) Udel® P-1700 polysulfone (PSU) is a tough, rigid, high-strength thermoplastics suitable for continuous use up to 300°F (149°C). It is resistant to oxidation and hydrolysis and withstand pro.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6 LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP 2C004 ETFE LNP* THERMOCOMP* 2C004 is a compound based on ETFE resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MF004S PP LNP THERMOCOMP* MF004S is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS LNP THERMOCOMP* NF002 is a compound based on PC+ABS resin containing 10% Glass Fiber. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min; ASTM D790 |
| A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min; ASTM D790 |
| A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min; ASTM D790 |
| A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Unitika TERRAMAC TE-2000 Polylactic Acid (PLA) Basic grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
| Flexural Strength | 106 MPa @Temperature 22.8 °C |
15400 psi @Temperature 73.0 °F |
ASTM D790 |
| Ensinger TECASON™ S Polysulfone (PSU) TECASON™ S is a transparent engineering plastic known for its chemical resistance, rigidity, high-temperature performance, and its ability to operate in an autoclave environment. TECASON™ S is FD.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Azoty Tarnow™ TARNOFORM 300 GF6 BK POM 30% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A... |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Ascend Performance Materials Vydyne® R513H Black Nylon 66, 13% Glass Reinforced, Conditioned Vydyne® R513H Black is general-purpose, 13% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is an injection-molding grade that is lubricated for machine feed, flow, and m.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Ashley Polymers Ashlene® 829 Nylon 6 Basic Nylon 6, low viscosity, unlubricated.Data provided by the manufacturer |
|||
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Azoty Tarnow™ TARNOFORM 300 MW4 POM Mineral filled injection molding grade based on Tarnoform 300 reinforced with 20% wollastonite; such a compound has high stiffness, dimensional stability and hardness combined with low shrinkage.Inf.. |
|||
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Ashley Polymers Ashlene® 828L Nylon 6 Medium viscosity general purpose nylon, complies with NSF under Standard 14 for pipe components.Data provided by the manufacturer |
|||