Quantum Polysulfone
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | Quantum Advanced Engineering Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quantum Polysulfone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 69 | 69 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Hardness, Shore D | 80 | 80 | ASTM 2240 |
| Tensile Strength | 70.3 MPa | 10200 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | ASTM D638 |
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | ASTM D790 |
| Compressive Strength | 95.8 MPa | 13900 psi | ASTM D695 |
| Shear Strength | 62.1 MPa | 9000 psi | ASTM D732 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.36 | 0.36 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.8 µm/m-°C | 31.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.252 W/m-K | 1.75 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 149 °C | 300 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 181 °C | 358 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+16 ohm-cm | 5.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.06 @Frequency 1.00e+6 Hz |
3.06 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 16.7 kV/mm | 425 kV/in | ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FDA Compliance | yes |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs P0P ABS, Plating Grade
- SABIC Innovative Plastics Lexan® SLX1432T PC Copolymer (Asia Pacific)
- Kolon ELLAS K-490AB Ester Based Thermoplastic Polyurethane
- Lubriplate Shield Gear Lithium Based Grease For Open Gearing
- LATI Latamid 66 H2 G/35-V0HF1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Trelleborg Emerson & Cuming Eccobond® 927-10 E Needle Bonding Epoxy Adhesive
- DSM Stanyl® TW200F8 Nylon 46-40% Glass Reinforced (European Grade) (Dry)
- Arkema Group Nakan® FKS 918 R PVC, Soft Extrusion Grade
- 3M Scotch-Weld™ EZ250060 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive
Copyright © lookpolymers.com All Rights Reserved