Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | >= 12.0 MPa | >= 1740 psi | Parallel to holes |
MarkeTech H-2 Honeycomb Ceramic MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo.. |
|||
Compressive Strength | >= 12.0 MPa | >= 1740 psi | Parallel to holes |
MarkeTech H-3 Honeycomb Ceramic MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo.. |
|||
Compressive Strength | >= 12.0 MPa | >= 1740 psi | Parallel to holes |
MarkeTech H-4 Honeycomb Ceramic MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo.. |
|||
Compressive Strength | 12.0 - 18.0 MPa | 1740 - 2610 psi | Cold Crushing Strength |
Gouda Vuurvast FI 25-15 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 12.0 - 18.0 MPa | 1740 - 2610 psi | Cold Crushing Strength |
Gouda Vuurvast FI 35-15 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 12.0 - 18.0 MPa | 1740 - 2610 psi | Cold Crushing Strength |
Gouda Vuurvast FI 45-15 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 12.0 MPa @Time 360000 sec |
1740 psi @Time 100 hour |
|
Wolf Kunststoff ZEDEX® ZX-100EL55 A1F Polymer Alloy, Elastomer Modified Main Characteristics: Rubbery; Soft; High shock absorption; High impact resistance; Elongation > 300%Applications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technol.. |
|||
Compressive Strength | 12.0 MPa @Time 360000 sec |
1740 psi @Time 100 hour |
|
Wolf Kunststoff ZEDEX® ZX-550 A5L Polymer Alloy Main Characteristics: Strong anti-adhesive; Low creep; Weather resistant; No water absorption; Good machinability; Strongly viscoelastic; Stress resistantApplications: Chemical Engineering; Laborato.. |
|||
Compressive Strength | 12.0 - 16.0 MPa | 1740 - 2320 psi | Cold Crushing Strength |
Gouda Vuurvast FI 25-12 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 12.0 - 16.0 MPa | 1740 - 2320 psi | Cold Crushing Strength |
Gouda Vuurvast FI 35-12 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | >= 12.0 MPa @Temperature 23.0 °C, Time 86400 sec |
>= 1740 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
Adamas Adalon® 305 PTFE, 15% Graphite Information provided by Adamas, HPM |