Adamas Adalon® 305 PTFE, 15% Graphite
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 305 PTFE, 15% Graphite.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.14 - 2.16 g/cc | 2.14 - 2.16 g/cc | ASTM D792 |
| Deformation | 5.0 - 5.5 % | 5.0 - 5.5 % | Permanent deformation after 24 hrs @ 23°C; ASTM D621 |
| 9.4 - 10.8 % | 9.4 - 10.8 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 52 - 56 | 52 - 56 | ASTM D2240 |
| Ball Indentation Hardness | 58.0 - 62.0 MPa | 8410 - 8990 psi | ISO 2032-N132 |
| Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ASTM D4894 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D4894 |
| Compressive Strength | >= 12.0 MPa @Temperature 23.0 °C, Time 86400 sec |
>= 1740 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
| Coefficient of Friction, Dynamic | 0.090 - 0.11 | 0.090 - 0.11 | ASTM D1894 |
| Coefficient of Friction, Static | 0.11 - 0.14 | 0.11 - 0.14 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 260 °C | 500 °F | DSC |
| Minimum Service Temperature, Air | -80.0 °C | -112 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+7 ohm | 1.00e+7 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® AD143 PC
- Covestro Apec® DP 1-9379/5 Polycarbonate (discontinued **)
- Honeywell Capran® 512 LL Heat Stabilized Nylon Film (discontinued **)
- Lehmann & Voss LUVOCOM® 1301-7767 PPS, linear, with carbon fiber, lubricant modified
- Zircar Zirconia YF-100 Yttria Felt Insulation
- ExxonMobil LLDPE LL 1001XV Wire & Cable Linear Low Density Polyethylene Resin (European Grade)
- Chosun Refractories APC-80G Acid-proof Castable
- DuPont Performance Polymers Hytrel® PC966 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
- Astaras Anviloy® Weld Rod
- Bulk Molding Compounds BMC 1423 Wear Resistant, Electrical Grade
Copyright © lookpolymers.com All Rights Reserved