- Polymer Property : Tensile Strength = 1000 psi
Polymer Property : Tensile Strength = 1000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
| Arlon R36798T017 0.017" (0.432 mm) Uncured Silicone Rubber with Laminated Tefzel® Substrate
(discontinue Design/Construction: Liner: PTFE Coated Fiberglass Side 1: Uncured Silicone Rubber Substrate: Laminated Tefzel® Substrate: Treated for adhesionAppearance: Translucent, high viscosity gum on fluoro.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
| Garlock 2102 C.I. SBR/NBR Sheet Rubber, Polyester Insert Garlock cloth-inserted materials are designed to add stability where mechanical fastening is necessary, and to reduce gasket creep where heavy flange loading is required.Style #2102 C.I. is a smooth.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
| Garlock 363 Nitrile Sheet Rubber Nitrile sheet is primarily used for applications where resistance to oil, solvents and fuels is required.Style #363 is a good quality, oil-resistant nitrile sheet.Information provided by Garlock Rub.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
| Garlock 567 EPDM Sheet Rubber Excellent general purpose gasket materials for air, hot and cold water, saturated steam and exterior service.Black, smooth finish, commercial qualityInformation provided by Garlock Rubber Technologi.. |
|||
| Tensile Strength | 6.89 - 20.7 MPa | 1000 - 3000 psi | ASTM D638, ASTM D1709 |
| Garlock 9405 PTFE Rubber Sheet, 25% Glass Filled Premium Grade 25% Glass-filled Skived PTFE SheetInformation provided by Garlock Rubber Technologies |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
| Garlock Viton® 501 Fluoroelastomer Sheet Rubber Style #501 sheet rubber, made with VITON® fluoroelastomer, is a high-performance product resistant to heat, oils, fuels, numerous acids and other chemicals.Information provided by Garlock Rubber .. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | |
| Garlock 660 Vegetable Fiber Gasketing Vegetable fiber with cork granules and glue-glycerin binder.Style 660 is designed for use in lightweight flanges and is compatible with water and most hydrocarbons.Information provided by Garlock Ru.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | ASTM F152 |
| Garlock 8316 EPDM Sheet Rubber Gasketing Ethylene propylene diene monomer (EPDM)FDA-approved. Recommended for service against aqueous foods.Information provided by Garlock Rubber Technologies |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | ASTM F152 |
| Garlock 9520 Fluoroelastomer Sheet Rubber Gasketing Fluoroelastomer (FKM) Type AExceptional resistance to heat, oils, fuels, numerous acids, and many other chemicals.Information provided by Garlock Rubber Technologies |
|||
| Tensile Strength | 6.90 MPa | 1000 psi | Flatwise |
| Henkel Hysol PL 795-1 Film Adhesive Tougher version of Hysol PL 795. Excellent flow characteristics. Excellent tack and handling characteristics. Improved elevated temperature performance. Can be used for both surfacing film and light.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | ASTM D412 |
| Saint-Gobain Tygon® Noroprene® Chemical Tubing Formulation Norprene® Chemical Tubing is a high performance co-extruded product specifically formulated to provide an ideal combination of chemical resistance and pump life. Its inert ultra-smooth plasticize.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon 10842S060 0.060" (1.52 mm) Fully Cured, Unsupported, Silicone Rubber Design/Construction:Side 1: Fully Cured, Unsupported, Silicone Rubber Appearance: Dark red silicone rubberThis data represents typical values for the production material. The data should not be used.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
| Arlon 10842S125 Cured/Post-cured, Unsupported Silicone Rubber Low ModulusProduct Color: Saddle BrownInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information pro.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property |
| Arlon 19606R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Prime Coated 1523 FiberglassSide 2: Uncured Silicone RubberInterleave: 0.003" PolyethyleneThis data represents typical values for the .. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
| Arlon 30400N085 0.085" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon 30400N125 0.125" (3.17 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured Unsupported Silicone Rubber on a Kodacel Carrier Appearance: Translucent silicone rubber on polymer linerThis data represents typical values for the production ma.. |
|||
| Tensile Strength | 6.89 - 8.27 MPa | 1000 - 1200 psi | Compound Property |
| Arlon 70011B016 0.016" (0.406 mm) Uncured Silicone Rubber with Prime Coated Polyester Fabric Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place .. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon CP-493C Bulk Compound This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Di.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon CP-494 Bulk Compound This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Di.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
| Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Design/Construction:Liner: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be us.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
| Arlon R30711R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave 1: PolyethyleneSide 1: Uncured Silicone Rubber Substrate: Style 1165 Fiberglass Side 2: Uncured Silicone Rubber Interleave 2: PolyethyleneAppearance: Red silicone gum .. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon R35061R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place .. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
| Arlon 30850S125 0.125" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property |
| Arlon 41940C020 0.015" Uncured, Unsupported Silicone Rubber on Release Carrier Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured, Unsupported Silicone RubberSubstrate: Holland Cloth CarrierThis data represents typical values for the production material and .. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon 51971R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber Appearance: Red gum on glass fiber fabricThis data Represents typical values for the production material. The data .. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon 55949C028 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber LayerSide 2: Uncured Silicone Rubber Appearance: Brown silicone rubber and gum on fiberglass clothThis data Represents typical values for the produc.. |
|||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Arlon R34260N005 0.005" (0.127 mm) Unsupported/Uncured Rubber with Fiberglass Substrate Design/Construction:Side 1: Unsupported/Uncured Rubber Appearance: Clear gum on release linersThis data Represents typical values for the production material. The data should not be used to write, o.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | ASTM D412 |
| Aaron Industries AAROPRENE® ATPR 1000 70A Elastomeric Compound AAROPRENE® ATPR 1000 Series Elastomeric CompoundDurometer values may be specified. Color may be specified. |
|||
| Tensile Strength | 6.90 MPa | 1000 psi | Flatwise |
| Henkel Hysol EA 9686 Film Adhesive Second generation, moisture resistant, toughened 250°F / 121°C curing film with service performance to 300°F / 149°C. Excellent for composite or metal bonding. Data from .060 psf, 300 g / m2.App.. |
|||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
| Arlon 43362X0055 0.0055" (0.140 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: PolyethyleneSide 1: Cured Silicone RubberSubstrate: Style 2112 FiberglassFlame Resistance: Product meets Title 14 CFR 25.856(a) Appendix F, Part VI (amdt. 25-111) fl.. |
|||