Arlon 30850S125 0.125" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 30850S125 0.125" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Thickness	127 microns	5.00 mil	Substrate
	3180 microns	125 mil	Rubber

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40	40	Silicone Property
Tensile Strength	>= 6.89 MPa	>= 1000 psi	Silicone Property
Elongation at Break	>= 700 %	>= 700 %	Silicone Property
100% Modulus	0.00103 GPa	0.150 ksi	Silicone Property
Tear Strength	>= 35.1 kN/m	>= 200 pli	Silicone Property
Compression Set	<= 28 %	<= 28 %	Silicone Property

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 177 °C	0.500 hour @Temperature 350 °F	Recommended Cure Cycle
	240 min @Temperature 227 °C	4.00 hour @Temperature 440 °F	Recommended Post Cure Cycle
Shelf Life	3.00 Month @Temperature 4.44 °C	3.00 Month @Temperature 40.0 °F

Descriptive Properties	Value	Comments
Color	Saddle Brown
Total Product Weight (oz/yd2)	105

Users viewing this material also viewed the following: