Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 6.89 MPa @Strain 100 % |
999 psi @Strain 100 % |
510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible A75M1 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible) This compound is certified for fuel hose applications(R1 Type B Class 1)under SAE J 1527 requirements.Information provided by PolyOne |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon R36798T017 0.017" (0.432 mm) Uncured Silicone Rubber with Laminated Tefzel® Substrate
(discontinue Design/Construction: Liner: PTFE Coated Fiberglass Side 1: Uncured Silicone Rubber Substrate: Laminated Tefzel® Substrate: Treated for adhesionAppearance: Translucent, high viscosity gum on fluoro.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Garlock 2103 C.I. SBR/NBR Sheet Rubber, Polyester Insert Garlock cloth-inserted materials are designed to add stability where mechanical fastening is necessary, and to reduce gasket creep where heavy flange loading is required.Style #2103 C.I. is a smooth.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Garlock 363 Nitrile Sheet Rubber Nitrile sheet is primarily used for applications where resistance to oil, solvents and fuels is required.Style #363 is a good quality, oil-resistant nitrile sheet.Information provided by Garlock Rub.. |
|||
Tensile Strength | 6.89 - 20.7 MPa | 1000 - 3000 psi | ASTM D638, ASTM D1709 |
Garlock 9405 PTFE Rubber Sheet, 25% Glass Filled Premium Grade 25% Glass-filled Skived PTFE SheetInformation provided by Garlock Rubber Technologies |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Typical |
Garlock Bay State 22 Natural/SBR Sheet Rubber Blend of natural and SBR rubber, specially compounded to be quick-sealing, non-hardening and heat resistant.Red, smooth rotocured finish. It conforms easily to uneven flange surfaces.Information pr.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | across grain; ASTM F152 |
Garlock MULTI-SWELLâ„¢ 3760 Compressed Aramid Fiber Gasketing Aramid fibers with a proprietary rubber binder.Creates compressive load in light weight flanges in oil and water serviceTwice as compressible as standard fiber gasketsSeals with low load and irregul.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM F152 |
Garlock 8314 EPDM Sheet Rubber Gasketing Ethylene Propylene Diene Monomer (EPDM)Resists weathering, ozone, and UV exposure.Information provided by Garlock Rubber Technologies |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM F152 |
Garlock 9518 Fluoroelastomer Sheet Rubber Gasketing Fluoroelastomer (FKM) Type AExceptional resistance to heat, oils, fuels, numerous acids, and many other chemicals.Information provided by Garlock Rubber Technologies |
|||
Tensile Strength | 6.89 MPa | 999 psi | |
Lucite International Elvacite ® 2043 Acrylic Resin Elvacite® 2043 is a low molecular weight ethyl methacrylate copolymer. It is a fast – dissolving, low viscosity resin with alcohol solubility for flexographic inks. Most compatible grade. It.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | |
Teknor Apex Tekbond® TB 1339A Thermoplastic Elastomer Notes: Tekbond® TPEs are a functional series of elastomer compounds designed to not only bond to the most difficult neat and reinforced engineering substrates with no primer or surface treatment, b.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Arlon 10842N125 Cured/Post-cured, Unsupported Silicone Rubber Low ModulusProduct Color: Natural (Transparent)Interleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Inform.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 10842S060 0.060" (1.52 mm) Fully Cured, Unsupported, Silicone Rubber Design/Construction:Side 1: Fully Cured, Unsupported, Silicone Rubber Appearance: Dark red silicone rubberThis data represents typical values for the production material. The data should not be used.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; Arlon SQA-TMS-008 |
Arlon 25188T020 0.020" Uncured Silicone Rubber/Laminated ETFE Film Design/Construction:Liner: 0.003" PTFE Coated FiberglassSide 1: Uncured Silicone RubberSubstrate: Laminated ETFE Film-treated for adhesionThis data represents typical values for the production ma.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 28941C015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data represents typical values for the production material. The data should not be used to write, or in place .. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
Arlon 30400N085 0.085" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
Arlon 41400R030 0.030" Uncured, Unsupported Silicone Rubber on a Release Carrier Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured, Unsupported Silicone RubberSubstrate: Holland Cloth CarrierThis data represents typical values for the production material and .. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon 51366X015 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: Polyethylene Side 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Flame Resistance: Product is designed to meet Title 14 CFR.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 55949C028W 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber LayerSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in pl.. |
|||
Tensile Strength | 6.89 - 8.27 MPa | 1000 - 1200 psi | Compound Property |
Arlon 70011B016 0.016" (0.406 mm) Uncured Silicone Rubber with Prime Coated Polyester Fabric Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place .. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon CP-494 Bulk Compound This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Di.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Design/Construction:Liner: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be us.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon R30711R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave 1: PolyethyleneSide 1: Uncured Silicone Rubber Substrate: Style 1165 Fiberglass Side 2: Uncured Silicone Rubber Interleave 2: PolyethyleneAppearance: Red silicone gum .. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon R37208T017 0.017" (0.432 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Liner Design/Construction: Liner: PTFE Coated Fiberglass Side 1: Uncured Silicone Rubber Substrate: Laminated Tefzel® Substrate: Treated for adhesionThis data represents typical values for the productio.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon 48362X005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 1080 FiberglassProduct Use: Flexible hose/duct substrateAppearance: Gray silicone rubber on fiberglass fabricThis data represents t.. |
|||
Tensile Strength | 6.89 - 8.27 MPa | 1000 - 1200 psi | Compound Property |
Arlon R33682C045 0.045" (1.14 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Infor.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon R33979C028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber Layer Side 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in p.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM D412 |
Aaron Industries AAROPRENE® ATPR 1000 70A Elastomeric Compound AAROPRENE® ATPR 1000 Series Elastomeric CompoundDurometer values may be specified. Color may be specified. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
Arlon 30850N125 0.125" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
Arlon 30850S085 0.085" Uncured, Unsupported Silicone Rubber on Release Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |