- PolyOne Geon™ Vinyl Flexible A75M1 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
PolyOne Geon™ Vinyl Flexible A75M1 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Flexible A75M1 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This compound is certified for fuel hose applications(R1 Type B Class 1)under SAE J 1527 requirements.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.019 - 0.023 cm/cm | 0.019 - 0.023 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | 15 sec; ASTM D2240 |
| 75 | 75 | ASTM D2240 | |
| Tensile Strength at Break | 14.5 MPa | 2100 psi | 510 mm/min; ASTM D638 |
| Tensile Strength | 6.89 MPa @Strain 100 % |
999 psi @Strain 100 % |
510 mm/min; ASTM D638 |
| Elongation at Break | 410 % | 410 % | 510 mm/min; ASTM D638 |
| Tear Strength | 64.8 kN/m | 370 pli | Die C, 510 mm/min; ASTM D624 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 79200 sec |
25 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 |
| Clash Berg Modulus | 0.689 GPa | 99.9 ksi | ASTM D1043 |
| 0.310 GPa @Temperature -22.0 °C |
45.0 ksi @Temperature -7.60 °F |
ASTM D1043 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -26.1 °C | -15.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % @Thickness 1.91 mm |
4.0 % @Thickness 0.0750 in |
ASTM D1003 |
| Transmission, Visible | 82 % @Thickness 1.91 mm |
82 % @Thickness 0.0750 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 177 - 182 °C | 351 - 360 °F | |
| 193 - 204 °C | 379 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Features | High Gloss | |
| Low to No Migration | ||
| Forms | Pellets | |
| Generic Material | PVC, Flexible | |
| Generic Name | Polyvinyl Chloride, Flexible (PVC, Flexible) | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Inno-Comp INNOPOL® CS 2-1000 Polypropylene Block-Copolymer
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours
- Star Plastics PC/PET7901 Molding Grade PC/PET
- A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6
- Dow AMPLIFY™ EA 103 Ethylene-ethyl Acrylate (EEA)
- DuPont Performance Polymers Zytel® SC315 NC010 Nylon 612 (Unverified Data**)
- ExxonMobil Mobil Delvac Coolant/Antifreeze Extended Life 50/50 Prediluted
- Ensinger TECASON™ S Polysulfone (PSU)
- 3M Dyneon™ Dynamar™ FX 5920B Polymer Processing Additive
- Polykemi AB POLYfill PPHC K8020 Polypropylene, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved