Arlon 41400R030 0.030" Uncured, Unsupported Silicone Rubber on a Release Carrier

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 41400R030 0.030" Uncured, Unsupported Silicone Rubber on a Release Carrier.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured, Unsupported Silicone RubberSubstrate: Holland Cloth CarrierThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
Physical Properties Metric English Comments
Thickness 127 microns
5.00 mil
Substrate
762 microns
30.0 mil
Silicone
Mechanical Properties Metric English Comments
Hardness, Shore A 55
55
Silicone Property
Tensile Strength >= 6.89 MPa
>= 1000 psi
Silicone Property
Elongation at Break >= 500 %
>= 500 %
Silicone Property
100% Modulus >= 0.00172 GPa
>= 0.250 ksi
Tension, Silicone Property
Tear Strength >= 35.1 kN/m
>= 200 pli
Silicone Property
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Processing Properties Metric English Comments
Cure Time 240 min

@Temperature 227 °C
4.00 hour

@Temperature 440 °F
Recommended Post Cure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 177 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 350 °F
Recommended Cure Cycle
Shelf Life 3.00 Month

@Temperature 4.44 °C
3.00 Month

@Temperature 40.0 °F
Descriptive Properties Value Comments
Color Naturally Translucent
Total Product Weight (oz/yd2) 28