Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics GELOY XP4025 ASA (Europe-Africa-Middle East) GELOY XP4025 is a high heat modified ASA/PC blend, for automotive exterior applications. It shows very good properties, gloss and colour retention, as well as faster cycle time over competitive mate.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 300 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Lexan® EX1332T PC (Europe-Africa-Middle East) LEXAN* EX1332T polycarbonate resin, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, extrusion, mold release, UV stabilized, transparent, translucent and opaque colors. Multiwall sheet, Profi.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 300 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Lexan® EX9332T PC (Europe-Africa-Middle East) LEXAN* EX9332T polycarbonate resin, MVR (300C/1.2kg) 3 cm3/10min, high viscosity, branched, extrusion, flame retadant, mold release, UV stabilized, transparent, translucent and opaque colors. Materi.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 1012/0001 Polyvinylidene Fluoride
(discontinued **) High molecular weight grade PVDFSuitable for compression molding or extrusionExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent stre.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 1012/1001 Polyvinylidene Fluoride
(discontinued **) High molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabilityInf.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics LNP LUBRICOMP DX09410H PC LNP* LUBRICOMP* DX09410H is a compound based on Polycarbonate resin containing Proprietary FIllers. Added features of this grade include: Healthcare, Wear Resistant. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 1.20 kg, Temperature 265 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® ENH8530 PBT+PET (Europe-Africa-Middle East) Non-Brominated & Non-Chlorinated Flame Retardant, 15% Glass fiber reinforced PBT/PET blend |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific) Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized |
|||
Melt Index of Compound | 5.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS01 3003 Enhanced White General Purpose Polystyrene PS01 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS01 range of resin co.. |
|||
Melt Index of Compound | 5.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS01 3009 Green General Purpose Polystyrene PS01 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS01 range of resin co.. |
|||
Melt Index of Compound | 5.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS01 Impact Modified Polystyrene 100% post-consumer recycled polymer (recovered from refrigerators)93% less CO2 impact compared with virgin*Successfully replaces virgin grade resinISO9000 quality certifiedAvailable in a range of co.. |
|||
Melt Index of Compound | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS02 1000 General Purpose Polystyrene PS02 Series polystyrenes offer the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS02 range of resin com.. |
|||
Melt Index of Compound | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS02 1010 Medium Impact Polystyrene PS02 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS02 range of resin co.. |
|||
Melt Index of Compound | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS02 Impact Modified Polystyrene 100% post-consumer recycled polymer (recovered from television casings)93% less CO2 impact compared with virgin*Successfully replaces virgin grade resinISO9000 quality certifiedAvailable in black/gr.. |
|||
Melt Index of Compound | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS13 1000 Impact Modified Polystyrene PS13 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS13 range of resin co.. |
|||
Melt Index of Compound | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS13 Impact Modified Polystyrene 100% post-consumer recycled polymer (recovered from coat hangers)93% less CO2 impact compared with virgin*Successfully replaces virgin grade resinISO9000 quality certifiedAvailable in black/greyCost.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 31508/0003 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 31508/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. PVDF 31508/0003 also has a very low brittleness temperature, for.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 32008/0009 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 32008/0009 is an ultra-flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 32008/0009 also has a very low brittleness te.. |
|||
Melt Index of Compound | 5.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS01 3000 General Purpose Polystyrene PS01 Series polystyrenes offer the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS01 range of custom co.. |
|||
Melt Index of Compound | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Spec |
Axion Polymers Axpoly® PS13 1011 High Impact Polystyrene PS13 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS13 range of resin co.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 31508/0001 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversation techniquesInformation provided by Dyneon, A .. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 32008/0003 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversion techniquesExcellent low flame and low smoke pe.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 31508/0009 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31508/0009 also has a very low brittleness temperatu.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 31008/0003 Polyvinylidene Fluoride
(discontinued **) 3M™ Dyneon™ PVDF 31008/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31008/0003 also has a very low brittleness temperatu.. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversation techniquesExcellent low flame and low smoke .. |
|||
Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversion techniquesInformation provided by Dyneon, A 3M.. |