Category	Polymer , Thermoplastic , Fluoropolymer , PVDF
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversion techniquesInformation provided by Dyneon, A 3M Company

Physical Properties	Metric	English	Comments
Density	1.76 g/cc	0.0636 lb/in³	ISO 1183
Water Absorption	<= 0.040 %	<= 0.040 %	24 hr @ 23°C; ISO 62 (method 1)
Melt Index of Compound	5.0 g/10 min @Load 2.16 kg, Temperature 230 °C	5.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
	15 g/10 min @Load 5.00 kg, Temperature 230 °C	15 g/10 min @Load 11.0 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	22.0 MPa	3190 psi	50mm/min; ASTM D638
Elongation at Break	475 %	475 %	50mm/min; ASTM D638
Flexural Modulus	0.200 GPa	29.0 ksi	2mm/min; ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	168 °C	334 °F	ASTM D3418
Brittleness Temperature	-37.0 °C	-34.6 °F	ASTM D746A
Oxygen Index	>= 44 % @Thickness 3.00 mm	>= 44 % @Thickness 0.118 in	Sheet; ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+14 ohm-cm	>= 1.00e+14 ohm-cm	10 mA, after 2 min; ASTM D257
Surface Resistivity per Square	>= 1.00e+14 ohm	>= 1.00e+14 ohm	< 1V after 2 min - 500 V; ASTM D257
Dielectric Constant	7.0 @Frequency 1e+6 Hz	7.0 @Frequency 1e+6 Hz	ASTM D150

Descriptive Properties	Value	Comments
Form	Pellets