Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer	Total Atofina
Trade Name	LDPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant. Grade for easy flow injection molding of flexible parts, powder production for grinding and master-batches.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.918 g/cc	0.918 g/cc	ISO 1183
Melt Flow	70 g/10 min @Load 2.16 kg, Temperature 190 °C	70 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	after 15 sec; ISO 868
Tensile Strength at Break	7.00 MPa	1020 psi	ISO 527-2
Tensile Strength, Yield	8.00 MPa	1160 psi	ISO 527-2
Elongation at Break	120 %	120 %	ISO 527-2
Modulus of Elasticity	0.150 GPa	21.8 ksi	ISO 527-2

Thermal Properties	Metric	English	Comments
Melting Point	105 °C	221 °F	ISO 11357
Vicat Softening Point	84.0 °C	183 °F	ISO 306
Shrinkage	2.0 - 4.0 %	2.0 - 4.0 %

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 220 °C	320 - 428 °F
Mold Temperature	30.0 - 40.0 °C	86.0 - 104 °F