Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
NOVA Chemicals Dylark® 378P30 Glass Reinforced Engineering Resin Features: Ultra high modulus, High heat resistance, excellent adhesion to urethaneApplications: Instrument panel substrates, Brackets, Structural components |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips HiD® 9640 HDPE Blown Film Resin
(discontinued **) Copolymerization Enhances Film Toughness, Unique Combination of Density and Melt Index, Excellent Strength Properties as well as Good Heat Seal, Lower Density Imparts a Softer Feel and Lesser Tenden.. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips HiD® 9647T HDPE Blown Film Resin
(discontinued **) Resin Type: Linear Polyethylene CopolymerCharacteristics: Copolymerization Enhances Film Toughness, Unique Combination of Density and Melt Index, Excellent Strength Properties as well as Good Heat S.. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | Exxon Method |
ExxonMobil Escorene® LD-701 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt, 10.5% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughnes.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips Marlex® HHM TR-418N/M358Y Natural medium density ethylene hexene copolymer/yellow concrete
( Benefits: environmentally-friendly pigment system, yellow color for easy identification, outstanding pipe rind ESCR, UV stabilizer in natural resin, concentrate base resinCharacteristics: Pipe Ring .. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 102-16 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 102-17 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 102-21 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 102-23 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 153-21 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 153-23 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® LP500200 High Density Polyethylene (Sheet & Profile Grade) ApplicationsThe PETROTHENE LP 5002 series of polyethylene resins exhibits excellent environmental stress crack resistance.Regulatory StatusThe LP 5002 base resin meets the requirements of Food and D.. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® LP500210 High Density Polyethylene (Sheet & Profile Grade) ApplicationsThe PETROTHENE LP 5002 series of polyethylene resins exhibits excellent environmental stress crack resistance.Regulatory StatusThe LP 5002 base resin meets the requirements of Food and D.. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
Hyosung Topilene R200P PP R200P Extrusion Random CopolymerApplications:Underfloor heating pipeWater service pipeCharacteristics:Pressure resistanceHigh impactLong-term heat stabilityFlexibilityInformation provided by Hyosung.. |
|||
Melt Flow | 0.20 - 0.28 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.20 - 0.28 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem GP 9452 F HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 153-17 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg |
0.20 g/10 min @Load 4.76 lb |
ISO 1133 |
SIDPEC EGYPTENE® HD 5502 GA HDPE Blow Molding Applications:Blow molded containers up to 30 liters for packagingChemicalsHousehold productsOils and foodstuffsInformation provided by Interchim s.r.l., official distributor of Sidi Kerir Petrochemi.. |
|||
Melt Flow | 0.20 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.20 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Borealis Borstar® FB1460 HDPE for Film Borstar FB1460 is a high-density polyethylene film grade, which combines superior physical properties with excellent processability. Due to the high density, the material properties are best utiliz.. |
|||
Melt Flow | 0.20 g/10 min @Load 5.00 kg, Temperature 90.0 °C |
0.20 g/10 min @Load 11.0 lb, Temperature 194 °F |
ISO 1133/T |
Total HDPE XLS 12 B High Density Polyethylene - Pipes and Fittings HDPE XLS 12 B is a high performance hexene-based black compound, with a MRS 10 MPa - PE100 classification, primarily intended for extrusion of large diameter and thick wall pressure pipes.Key charac.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips MarFlex® HHM TR-258 Low Density Linear Polyethylene, Blown Film This LDLPE is tailored for applications that require:Good processabilityGood melt strengthGood drawdownGood strengthSatin finishGood MD & TD shrinkageGood contact clarity and lower gel contentTypica.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips Marlex® HHM TR-418Q MDPE Hexene Copolymer High performance MDPE resin has been formulated for the demanding requirements of pressure pipe applications. Meets ASTM D4976 PE 225. Meets FDA Regulation 177.1520, suitable for food packaging ap.. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
Aclo Accutech Polyethylene HD0232G20CV High Density Glass Reinforced Chemically Coupled Approved to GMP.PE.018 Black A12438 |
|||
Melt Flow | 0.20 - 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 - 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene HD Bottles Flakes High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
Aclo Accutech ABS ABS834G40L Glass Reinforced |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | I<sub>2</sub>; ASTM D1238 |
Petromont 7001 Medium Density Polyethylene Resin Petromont HDPE 7001 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is designed to be readily processed by flat die extrusi.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis LE6022 Polyethylene Modified Jacketing Compound LE6022 is a black low density copolymer modified polyethylene compound. It is characterized by excellent crack resistance and mechanical properties and low temperature performance in combination wit.. |
|||
Melt Flow | 0.20 - 0.50 g/10 min | 0.20 - 0.50 g/10 min | |
Kazanorgsintez 153-16 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Paxon™ AA50-002 Blow Molding Resin
(discontinued **) AA50-002 is a blow molding grade high density polyethylene. This resin has excellent stress crack resistance combined with high impact strength, rigidity, and melt strength.Information provided by .. |
|||
Melt Flow | 0.20 g/10 min | 0.20 g/10 min | I<sub>2</sub>; ASTM D1238/E |
Petromont 7002 Medium Density Polyethylene Resin Petromont HDPE 7002 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is designed to be readily processed by flat die extrusi.. |
|||
Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Formosa Plastics Formolene® HP3902 Pipe HDPE Natural Medium Density Hexene CopolymerApplications: Pipe for gas distribution, oilfield and other industrial pipe, telecommunications conduit.Formolene HP3902 is a high performance copolymer that i.. |