Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.2 - 2.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
1.2 - 2.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Polyplastic Armoflen® PO MF 65-3 Polyethylene, 65% Mineral Filled 50% Calcium Carbonate / 15% Titanium Oxide FilledInformation provided by PolyPlastic Group. |
|||
Melt Flow | 1.5 - 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.5 - 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 4240G (EP2S29B) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Melt Flow | 1.0 - 2.0 g/10 min | 1.0 - 2.0 g/10 min | |
Kazanorgsintez 107-18 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 1.0 - 2.0 g/10 min | 1.0 - 2.0 g/10 min | |
Kazanorgsintez 107-19 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 1.0 - 2.0 g/10 min | 1.0 - 2.0 g/10 min | |
Kazanorgsintez 107-20 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 1.0 - 2.0 g/10 min | 1.0 - 2.0 g/10 min | |
Kazanorgsintez 107-22 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Melt Flow | 1.5 - 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.5 - 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Kazanorgsintez PE2NT74-15 High Density Polyethylene for Blow Molding Production Method: Gaseous-phase method. Application: Compositions are intended for goods produced by injection molding method.Information Provided by Kazanorgsintez |
|||
Melt Flow | 1.8 - 2.0 g/10 min @Load 2.61 kg, Temperature 190 °C |
1.8 - 2.0 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical SEETEC BF410 LDPE Characteristics: Good Processability and Excellent Optical PropertiesAdditives: Antiblocking Agent, Slip AgentApplications: Industrial Film & Food PackageCAS No. 9002-88-4Information provided by LG .. |
|||
Melt Flow | 1.6 - 2.0 g/10 min @Load 2.61 kg, Temperature 190 °C |
1.6 - 2.0 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical SEETEC BF415 LDPE Characteristics: Good Processability and Excellent Optical Properties Applications: Masking filmCAS No. 9002-88-4Information provided by LG Chemical |
|||
Melt Flow | 1.0 - 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.0 - 2.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
GRECO ISOPAK 525 ABS Resin General Purpose Injection GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd. |
|||
Melt Flow | 0.80 - 2.0 g/10 min | 0.80 - 2.0 g/10 min | |
Shandong Dongyue Shenzhou New Material Co DS602 Perfluorinated Ethylene-Propylene Copolymer Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and.. |
|||
Melt Flow | 0.80 - 2.0 g/10 min | 0.80 - 2.0 g/10 min | |
Shandong Dongyue Shenzhou New Material Co DS606 Fluorinated Ethylene Propylene Powder Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene powder is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, an.. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |