Polymer Property : Apparent Bulk Density = 0.0217 lb/in³ Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³	ISO 60
Raschig Group MELOPAS® 156 MF Melamine Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200..
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³	ISO 60
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu..
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³	ISO 60
Raschig Group RESINOL® 87120 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets ..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ISO 60
Hexion Bakelite™ PF 31.5 Phenolic Formaldehyde Resin, Improved Electrical Properties (discontinued **) Phenolic molding compound, mainly organically filled, electrically high grade, standardized molding compound.Application areas: Parts for electrical and telecommunications technology, car electronic..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ISO 60
Hexion Bakelite™ PF 31.9 Phenolic Formaldehyde Resin, Ammonia Free (discontinued **) Phenolic molding compound, mainly organically filled, ammonia free, standardized molding compound.Application areas: Parts for electrical and telecommunications technology, motor vehicle ignition sy..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ISO 60
Hexion Bakelite™ X24 Phenolic Formaldehyde Resin (discontinued **) Phenolic molding compound, mainly organically filled.Application areas: Operating controls, housing parts, lamp holders.Information provided by Bak AGBak AG became a part of Hexion in 2005.
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ASTM D1895
Plenco 201 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound (discontinued **) Plaslok 201 is a two-stage, woodflour and mineral-filled phenolic molding compound formulated to have an excellent balance of molded properties. The material provides good electrical insulation val..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ASTM D1895
Plenco 504 Black (COM) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound (discontinued **)< Plaslok 504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding compounds. Since it also has good electrical..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/inÂ³	ASTM D1895
Solvay Specialty Polymers Catalyst CT/4 BLK Polyolefin Catalyst CT/4 BLK is a polyolefin based masterbatch to be used with cable silane crosslinkable compounds in the amount suggested for each material. Developed for PolidanÂ®, PolidiemmeÂ® and Coge..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/inÂ³	ISO 60
Styron MAGNUMâ„¢ 3325 MT Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 3325 MT is a resin with excellent processing characteristics and matt surface finish. The mass (continuous process) ABS technology of Styron ensures an ABS resin that combines..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/inÂ³	ASTM D1895
Sumitomo Bakelite DurezÂ® 153 Phenolic, Compression Grade Durez 153 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits good molded appearance and shock resistance for use on a wide variety of electrical a..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³
Tipco Megabatch® MD 3220 LLDPE based Metal De-Activator Masterbatch 20% Metal De-Activator (Cu-Inhibitor) Masterbatch in LLDPEApplications: General PurposeProcessing: Injection & ExtrusionInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³
Tipco Megabatch® UV 1022 Polypropylene based UV Stabilizer Masterbatch 20% UV Stabilizer (polymeric-HALS) Masterbatch in PP HomopolymerApplications: General PurposeProcessing: Injection & ExtrusionInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	TRM-37
Tipco Tipcolene® MD 3220 - Metal Deactivator (20% Copper Inhibitor) Masterbatch in LLDPE
Apparent Bulk Density	0.600 - 0.620 g/cc	0.0217 - 0.0224 lb/in³	ISO 60
Tisan TISMOSET® Properties:Flame retardantHigh gloss surfaceImproved thermal and electircal strengthHigh impact strengthMinimized shrinkage at the presence of moldingHigh melting flow indexReduced moisture absorpti..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³
Cytec Thornel® Mat VME Carbon Fiber Data provided by the manufacturer, Amoco Performance Products, Inc.Form of mat VMA with shorter fibers for injection molding. Fiber lengths average 200 µm - inadequate for good mechanical property..
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³
Domo Domamid® 24 Polyamide 6 DOMAMID® 24 are a low viscous Polyamide 6 pellets produced from Caprolactam by polymerization. Applications: Textile yarn extrusionCompounding Injection moulding Information provided by Domo
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³
Domo Domamid® 24 T Polyamide 6 DOMAMID® 24 T are a low viscous Polyamide 6 pellets produced from Caprolactam by polymerization. Domamid T products are special textile grades with a high uniformity of relative viscosity and Amino..
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³
Domo Domamid® 32 Polyamide 6 DOMAMID® 32 are Polyamide 6 pellets with a higher viscosity produced from Caprolactam by polymerization.Applications: Standard quality for production of monofilaments and fishing netsInformation pr..
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³
Domo Domamid® 33 Polyamide 6 DOMAMID® 33 are Polyamide 6 pellets with a higher viscosity produced from Caprolactam by polymerization. Applications: Standard quality for production of monofilaments and fishing netsInformation p..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	Tap density
Carborundum CarboTherm™ CTL30 Boron Nitride Powder Boron Nitride powders have high thermal conductivity, low dielectric loss, and low thermal expansion. They are non-abrading to electronic components, lubricious, non-toxic, and retain their dielect..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	Tap density
Carborundum CarboTherm™ CTUF Boron Nitride Powder Boron Nitride powders have high thermal conductivity, low dielectric loss, and low thermal expansion. They are non-abrading to electronic components, lubricious, non-toxic, and retain their dielect..
Apparent Bulk Density	0.600 - 0.660 g/cc	0.0217 - 0.0238 lb/in³	IS 867-1963
Amity Thermosets ATI 102 Phenolic Molding Organic Filler, Injection Molded Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-blackVery soft flow Applications: Electric swit..
Apparent Bulk Density	0.600 - 0.680 g/cc	0.0217 - 0.0246 lb/in³	IS 867-1963
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Injection Molded Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft flow Applications:Telecommunication ..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³
Arkema Group Lacovyl® GB 9010 M PVC LACOVYL GB 9010 M is a low molecular weight vinyl chloride homopolymer produced by mass polymerization process using the Elf Atochem's latest technology.Its characteristics are : Viscosity inde..
Apparent Bulk Density	0.600 - 0.800 g/cc	0.0217 - 0.0289 lb/in³	ISO 60
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets ..
Apparent Bulk Density	0.600 - 0.860 g/cc	0.0217 - 0.0311 lb/in³	Average value: 0.732 g/cc Grade Count:6
Overview of materials for Diallyl Phthalate (DAP), Cast, Mineral Filler This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP), Cast, Mineral Filler". Each property range of values reported is minimum and ma..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ASTM D1895
Plaslok 7000 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 7000 is the replacement material for ..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ASTM D1895
Plaslok 504 Black (COM) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound (discontinued **)&l Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 504 is a two-stage, mineral and cellu..
Apparent Bulk Density	0.600 g/cc	0.0217 lb/in³	ASTM D1895
Plaslok 504 Black (INJ) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound (discontinued **)&l Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 504 is a two-stage, mineral and cellu..