Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® PP 1385 PRE-ELEC PP 1385 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PP CQX30030 RTX Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PP EIP2012 F Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PPC T1010 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PPH 150DNH Polypropylene Homopolymer, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | With Flow; ISO 2577 |
Polykemi AB POLYfill PPHC K3020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PPHC K3020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ASTM D955 |
Polymer Resources TP-FR-IM Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low Flow Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sa.. |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYelast TPE R44 T10 Thermoplastic Elastomer, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | With Flow; ISO 2577 |
Polykemi AB POLYelast TPE R44 T10 Thermoplastic Elastomer, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | With Flow; ISO 2577 |
Polykemi AB POLYfill PPH B8065 VT1 Polypropylene Homopolymer, Mineral Reinforced, Heat Resistant Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.0050 - 0.014 cm/cm | 0.0050 - 0.014 in/in | FRISETTA Test Method |
Nilit FRIANYL A63 H-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.0050 - 0.014 cm/cm | 0.0050 - 0.014 in/in | FRISETTA Test Method |
Nilit FRIANYL A63 H-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm @Thickness 3.20 mm, Time 259000 sec |
0.0090 - 0.014 in/in @Thickness 0.126 in, Time 72.0 hour |
ASTM D955 |
A. Schulman POLYPUR™ CB 1110 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm @Thickness 3.20 mm, Time 259000 sec |
0.0090 - 0.014 in/in @Thickness 0.126 in, Time 72.0 hour |
ASTM D955 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.0040 - 0.014 cm/cm @Thickness 3.175 mm |
0.0040 - 0.014 in/in @Thickness 0.1250 in |
ASTM D955 |
A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ISO DIS 294-4 |
Wellman EcoLon® MRGF1619-WBK1 Mineral and Glass Reinforced Recycled Nylon 66 Description: Post Consumer Nylon Compound; WeatherableInformation provided by Wellman. |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D 955 |
Cossa Polimeri ESTAPROP H 1040 TG Polypropylene, 20% Mineral Filled PP homopolymer 20% mineral fillerGood physical and mechanical characteristics, good processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D955 |
Buckeye Polymers BP RPP 1012 T BLK Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PP 150ENH Polypropylene, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | With Flow; ISO 2577 |
Polykemi AB POLYfill PP 150ENH Polypropylene, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PPHC K9020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm @Thickness 3.20 mm, Time 259000 sec |
0.0090 - 0.014 in/in @Thickness 0.126 in, Time 72.0 hour |
ASTM D955 |
A. Schulman POLYPUR™ CB 1110 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D955 |
A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene DescriptionPolyflam® RPP 1360 is a UL 94 V0 rated, non-halogenated homopolymer polypropylene flame retardant compound. Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ASTM D955 |
Solvay Engineered Polymers SEQUEL® E2200 TPO
(discontinued **) Description: SEQUEL® E2200 thermoplastic olefinic elastomer (TPO) is designed for thermoformed exterior and interior applications that require low-temperature toughness and high rigidity. This pro.. |