The NanoSteel® Company SHS 9192 GMAW OAW Steel Alloy, Cored Wire

Category	Metal , Ferrous Metal , Alloy Steel , Other Engineering Material , Ceramic/Metallic Coating
Manufacturer	The NanoSteel® Company
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	The NanoSteel® Company SHS 9192 GMAW OAW Steel Alloy, Cored Wire.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Coating Description: SHS 9192 GMAW OAW is an iron based steel alloy with a near nanoscale (submicron) microstructure that features extreme abrasion resistance with high toughness, high volume of hard phases and superior high temperature hardness. SHS 9192 is an alternative to chrome and tungsten carbides.Key Performance Characteristics69 - 72 HRc single and double pass weld depositsExtreme resistance to abrasion while maintaining high toughnessAlternative weld material to tungsten carbides, chrome carbides, complex carbides, stick weld material loaded with carbides, and tungsten carbide laden Teflon® sheet overlaysMaintains high hardness after exposure to high temperaturesApplication Process: GMAW OAW Weld Overlay for HardfacingInformation Provided by The NanoSteel Company, Inc.

Physical Properties	Metric	English	Comments
Density	7.68 g/cc	0.277 lb/in³	Weld Deposit Property

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	69 - 72	69 - 72

Component Elements Properties	Metric	English
Aluminum, Al	<= 5.0 %	<= 5.0 %
Boron, B	<= 5.0 %	<= 5.0 %
Carbon, C	<= 5.0 %	<= 5.0 %
Chromium, Cr	<= 20 %	<= 20 %
Iron, Fe	>= 28 %	>= 28 %
Manganese, Mn	<= 5.0 %	<= 5.0 %
Molybdenum, Mo	<= 10 %	<= 10 %
Niobium, Nb (Columbium, Cb)	<= 10 %	<= 10 %
Silicon, Si	<= 2.0 %	<= 2.0 %
Tungsten, W	<= 10 %	<= 10 %

Descriptive Properties	Value	Comments
Impact Resistance	Passed multiple impacts at 165 ft-lbs	Drop Impact Testing
Wear Resistance Mass Loss (g)	0.06-0.14	6000 cycles; ASTM G65-04 Procedure A