Styron CALIBREâ„¢ 5101-8 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 5101-8 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ 5101 Polycarbonate resins 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.Main Characteristics:Glass reinforcedIgnition resistantISO 10993Applications:Information Technology EquipmentTelecommunicationsMedical applicationsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183/B; ASTM D792
Water Absorption 0.25 %

@Temperature 23.0 °C
0.25 %

@Temperature 73.4 °F
Equilibrium, 50% RH; ISO 62; ASTM D570
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ISO 294-4; ASTM D955
Melt Flow 8.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 62
62
ASTM D785
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength at Break 60.7 MPa
8800 psi
50 mm/min; ASTM D638
61.0 MPa
8850 psi
ISO 527-2/50
Tensile Strength, Yield 62.0 MPa
8990 psi
ISO 527-2/50
62.1 MPa
9010 psi
50 mm/min; ASTM D638
Elongation at Break 6.0 %
6.0 %
50 mm/min; ISO 527-2/50; ASTM D638
Tensile Modulus 3.38 GPa
490 ksi
ISO 527-2/50; ASTM D638
Flexural Strength 93.8 MPa
13600 psi
Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Flexural Modulus 3.17 GPa
460 ksi
Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Izod Impact, Notched (ISO) 80.0 kJ/m²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
ASTM D256
Tensile Impact Strength 147 kJ/m²
69.9 ft-lb/in²
ASTM D1822
Dart Drop, Total Energy 40.1 J
29.6 ft-lb
3.39 m/sec; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C

@Temperature -40.0 - 82.0 °C
37.8 µin/in-°F

@Temperature -40.0 - 180 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Annealed; ISO 75-2/B; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 134 °C
273 °F
Unannealed; ISO 75-2/A; ASTM D648
Vicat Softening Point 160 °C

@Load 5.10 kg
320 °F

@Load 11.2 lb
Rate A (50°C/h); ISO 306/B50; ASTM D1525
Flammability, UL94 V-2

@Thickness 1.59 mm
V-2

@Thickness 0.0626 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Oxygen Index 32 %
32 %
ISO 4289-2
Descriptive Properties Value Comments
Average Extent of Burring 1 cm
ASTM D635