PolyOne Syncure™ System S120NA Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer PolyOne Corporation
Trade Name Syncure™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Syncure™ System S120NA Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Syncure™ systems are two part moisture crosslinkable compounds. S120NA is suitable for applications requiring high density, high rigidity and operating temperatures up to 125°C. RoHS compliant.NOTE: The above represents Typical Properties measured on 14 AWG with 30 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.948 g/cc
0.948 g/cc
ASTM D792
Oxidative Induction Time (OIT) 40 min
40 min
ASTM D3895
Deformation 10 %

@Temperature 131 °C,
Time 3600 sec
10 %

@Temperature 268 °F,
Time 1.00 hour
500 g; UL 1581
Mechanical Properties Metric English Comments
Hardness, Shore D 59
59
10 sec; ASTM D2240
64
64
ASTM D2240
Tensile Strength, Yield 31.0 MPa
4500 psi
Type IV, 510 mm/min; ASTM D638
Elongation at Break 30.0 %
30.0 %
SYV-40; Hot Creep Elongation
80 %
80 %
Type IV, 510 mm/min; ASTM D638
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
UL Temperature Rating
Electrical Properties Metric English Comments
Dielectric Constant 2.1

@Frequency 1.00e+6 Hz
2.1

@Frequency 1.00e+6 Hz
ASTM D150
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Appearance Natural Color
Catalyst Masterbatch 5%
S-1037B
Forms Pellets
Gel Content 72%
ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material XLPE
Generic Name Polyethylene, Crosslinked (XLPE)
Grafted Base Resin 95%
S1016A
Processing Method Extrusion Coating
Regional Availability North America
Retention of Tensile Elongation 75%
121°C, 1.91 mm; 336 hr, UL Standard
Retention of Tensile Strength 75%
121°C, 1.91 mm; 336 hr, UL Standard
Uses Appliances
Wire & Cable Applications