Hexcel® HexWeb® CR III 3/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb

Category Metal , Metal Foam, Mesh, or Honeycomb , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Hexcel
Trade Name HexWeb®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® CR III 3/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR III coating has been developed to offer superior protection for aluminum honeycomb exposed to corrosive environments. The HexWeb CR III system offers a clear protective film that interacts with the aluminum surface forming a stable, tightly adherent bond. The coating is primarily in an organo-metallic polymer type that differs from the normal conversion-type corrosion protective coatings.Hexcel expanded honeycomb is manufactured by bonding together sheets of aluminum foil, then expanding to form a cellular honeycomb confiation. Resulting panels have sharp, clean cell walls, are essentially burr-free, and are suitable for high-quality core-to-facing bond.Aluminum HexWeb CR III Specification Grade honeycomb materials are predominantly used in sandwich structures to meet design requirements for highly engineered structural components. As a structural core material it finds applications in all types of aerospace vehicles and supporting equipment where sandwich structure offers rigid panels of minimum weight, aerodynamic smooth surfaces, and high fatigue resistance. The same structural properties are also used for commercial applications such as tools, snow and water skis, bulkheads, and floors. Other nonstructural uses are direction air/fluid flow control, RF shielding, and energy absorption.
Physical Properties Metric English Comments
Density 0.0336 g/cc
0.00122 lb/in³
Nominal
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.621 MPa
>= 90.0 psi
Bare, min
>= 0.689 MPa
>= 100 psi
Stabilized, min
1.10 MPa
160 psi
Bare, typ
1.21 MPa
175 psi
Stabilized, typ
Compressive Modulus 0.234 GPa
34.0 ksi
Stabilized, typ
Shear Modulus 0.0986 GPa
14.3 ksi
Plate Shear, W Direction, typ
0.186 GPa
27.0 ksi
Plate Shear, L Direction, typ
Shear Strength >= 0.317 MPa
>= 46.0 psi
Plate Shear, W Direction, min
0.483 MPa
70.0 psi
Plate Shear, W Direction, typ
>= 0.552 MPa
>= 80.0 psi
Plate Shear, L Direction, min
0.827 MPa
120 psi
Plate Shear, L Direction, typ