Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, AS4-C

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, AS4-C.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiber Designation: C193PW, Plain weaveInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 820 MPa

@Temperature 23.0 °C
 119000 psi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D3039
Tensile Modulus 61.0 GPa

@Temperature 23.0 °C
 8850 ksi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D3039
Flexural Yield Strength 549 MPa

@Temperature 90.0 °C
 79600 psi

@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D790
934 MPa

@Temperature 23.0 °C
 135000 psi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D790
Flexural Modulus 50.0 GPa

@Temperature 23.0 °C
 7250 ksi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D790
55.0 GPa

@Temperature 90.0 °C
 7980 ksi

@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D790
Compressive Yield Strength 461 MPa

@Temperature 90.0 °C
 66900 psi

@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D965
649 MPa

@Temperature 23.0 °C
 94100 psi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D965
Shear Strength 38.0 MPa

@Temperature 90.0 °C
 5510 psi

@Temperature 194 °F
 0°, Interlaminar, Conditioning: 23°C; ASTM D2344
40.0 MPa

@Temperature 60.0 °C
 5800 psi

@Temperature 140 °F
 0°, Interlaminar, Conditioning: 60°C-90% RH; ASTM D2344
64.0 MPa

@Temperature 23.0 °C
 9280 psi

@Temperature 73.4 °F
 0°, Interlaminar, Conditioning: 23°C; ASTM D2344
Processing Properties Metric English Comments
Shelf Life 12.0 Month

@Temperature -18.0 °C
 12.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Dry Resin Content (%) 42
Fiber Volume (%) 49.5