ExxonMobil Paxon™ BA7718 Sheet Extrusion and Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Paxon™ BA7718 Sheet Extrusion and Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BA7718 is a 25% brown mica-filled, medium molecular weight, high density polyethylene. This material has been specifically developed as a cost effective resin for applications which require outstanding stiffness and heat deflection temperatures. This material is designed for increased rigidity, dimensional stability, warpage resistance, and heat deflection temperatures compared to conventional HDPE. Resin must be dried just prior to the blow molding or sheet extrusion process.Information provided by ExxonMobil Chemical

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	73	73	15s; ASTM D2240
Tensile Strength at Break	37.2 MPa	5400 psi	ASTM D638
Tensile Strength, Yield	42.1 MPa	6100 psi	ASTM D638
Elongation at Break	7.0 %	7.0 %	ASTM D638
Elongation at Yield	6.0 %	6.0 %	ASTM D638
Flexural Modulus	2.62 GPa	380 ksi	Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790
Gardner Impact	22.6 J @Temperature 23.0 °C	16.7 ft-lb @Temperature 73.4 °F	ASTM D3029
Tensile Impact Strength	52.5 kJ/m²	25.0 ft-lb/in²	ASTM D1822

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	99.0 °C	210 °F	ASTM D648