Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882 |
DuPont Teijin Films Mylar® M45 Polyester Film, 50 Gauge (15 µm), PVDC Coated
(discontinued **) Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, dispersion coated on one side with a PVDC copolymer. The coating is an excellent moisture and oxygen barrier. M45.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte® 70 MET OPP Film Product Description: A moderate barrier, metalized OPP film for use in adhesive and extrusion laminations to reveres-printed outer webs. The proprietary broad seal range layer offers excellent hot t.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte® 70 MET-HB OPP Film Product Description: A vacuum-metallized, high barrier OPP film with a proprietary sealant layer. This film offers excellent moisture and oxygen barriers, hot tack, seal integrity, and lap seal rang.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 1000 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 1400 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 200 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 380 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 500 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 700 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 75 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329 Polyester Film, 92 Gauge Melinex® 329 is an opaque white, non-pretreated, polyester film with good handling properties and a unique glossy appearance. It is used as a base for pressure sensitive labels, in security and ac.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 329W Polyester Film, 300 Gauge An opaque white film with good handling properties and a unique glossy appearance. 329W has same properties as 329 with the only exception being it is wound reverse. See the 329 datasheet for detail.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 339 Polyester Film, 300 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 33.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 339 Polyester Film, 700 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 339 Polyester Film, 820 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 547 Polyester Film, 400 Gauge Information provided by DuPont. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® ST328 Polyester Film, 1400 Gauge Melinex® ST328 is an exceptionally white, opaque film with a satin finish. It is pretreated on both surfaces to promote adhesion to a wide range of solvent-based and UV-curable graphics inks and va.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® C Polyester Film, 10 Gauge Mylar® Type C films are available in a wide range of generally thinner gauges (typically 10 through 92) that offer excellent electrical properties, combined with superior strength and dimensional s.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LJP Polyester Film, 1000 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LJP Polyester Film, 500 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LJP Polyester Film, 650 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® P25 Polyester Film, 75 Gauge Product Description: Mylar® P25 is an uncoated, transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. S.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® TL Polyester Film Mylar® Type TL film is a film specified for card protection engineered to provide an identical shrinkage between MD/TD and also possessing good properties of resistance to moisture, oils and chemic.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 339 Polyester Film, 500 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 340 Polyester Film, 200 Gauge Melinex® 340 is an opaque white polyester film with good handling properties that is not treated on either surface.Typical Applications: Melinex® 340 is used as a base for pressure sensitive label.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882 |
DuPont Teijin Films Mylar® M45 Polyester Film, 75 Gauge (22 µm), PVDC Coated
(discontinued **) Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, dispersion coated on one side with a PVDC copolymer. The coating is an excellent moisture and oxygen barrier. M45.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 339 Polyester Film, 200 Gauge Melinex® 339 is an opaque white polyester film with good handling properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings.Typical Applications: Melinex® 339.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LJP Polyester Film, 200 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LJP Polyester Film, 300 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us.. |
|||
Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 343 Polyester Film, 200 Gauge Melinex® 343 is an opaque white polyester film with good handling properties that is treated on one surface to promote adhesion to most industrial coatings.Typical Applications: Melinex® 343 is us.. |