Advanced Polymer Alloys Alcryn® 2165 NC Melt Processable Rubber

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer	APA - Advanced Polymer Alloys
Trade Name	Alcryn®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Advanced Polymer Alloys Alcryn® 2165 NC Melt Processable Rubber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Alcryn 2100 Series melt-processable rubber (MPR) offer a broader range of bonding to rigid substrates while maintaining all the excellent performance features of traditional Alcryn. The 2100 grades bond to polycarbonate, ABS, polycarbonate/ABS alloys, SAN, ASA, copolyester elastomers and TPUs, as well as both flexible and rigid PVC. Applications:Injection-molded and overmolded partsSoft touch handles and gripsAutomotive interior applicationsSeals and gaskets for automotive insert moldingNoise and vibration deadeningBlow-molded partsTubing and hoseWire and cable jacketsCoated fabrics and sheet goodsWindow and door weatherstrippingInformation provided by Advanced Polymer Alloys

Physical Properties	Metric	English	Comments
Specific Gravity	1.40 g/cc	1.40 g/cc	ASTM D471; ISO 2781; DIN 53479
Viscosity	232000 cP @Shear Rate 300 1/s, Temperature 190 °C	232000 cP @Shear Rate 300 1/s, Temperature 374 °F	ASTM D3835

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	66	66	ASTM D2240; ISO 48; DIN 53505
Tensile Strength, Ultimate	0.662 MPa	96.0 psi	After 7 days at 257°F (125°C); ASTM D573; ISO 188; DIN 53508
	11.7 MPa	1700 psi	ASTM D412; ISO 37; DIN 53504
Elongation at Break	91 %	91 %	After 7 days at 257°F (125°C); ASTM D573; ISO 188
	570 %	570 %	ASTM D412; ISO 37; DIN 53504
100% Modulus	0.000752 GPa	0.109 ksi	After 7 days at 257°F (125°C); ASTM D573; ISO 188; DIN 53508
	0.00300 GPa	0.435 ksi	ASTM D412; ISO 37; DIN 53504
Graves Tear Strength	38.6 kN/m @Temperature 23.9 °C	220 pli @Temperature 75.0 °F	Die C; ASTM D624; DIN 53507
Compression Set	34 %	34 %	After 22 Hr at 75°F (24°C); ASTM D395; ISO 815; DIN 53517
	83 % @Temperature 100 °C	83 % @Temperature 212 °F	22 hrs.; ASTM D395; ISO 815; DIN 53517
Tensile Set	13 %	13 %	ASTM D412

Processing Properties	Metric	English	Comments
Processing Temperature	177 °C	350 °F

Descriptive Properties	Value	Comments
Fluid Resistance - Volume Change, % (ASTM D471)	-16	After 7 Days in ASTM Oil No.1 at 212°F (100°C)
	19	After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C)
	9	After 7 Days in IRM 903 Oil No.3 at 212°F (100°C)