Polymer Property : Specific Heat Capacity = 0.427 J/g-Â°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Specific Heat Capacity	0.427 J/g-Â°C @Temperature 100 Â°C	0.102 BTU/lb-Â°F @Temperature 212 Â°F
Haynes HastelloyÂ® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Specific Heat Capacity	0.427 J/g-Â°C @Temperature 100 Â°C	0.102 BTU/lb-Â°F @Temperature 212 Â°F
Haynes HastelloyÂ® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649Â°C (1200Â°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Specific Heat Capacity	0.427 J/g-°C @Temperature 100 °C	0.102 BTU/lb-°F @Temperature 212 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Specific Heat Capacity	0.427 J/g-°C @Temperature 100 °C	0.102 BTU/lb-°F @Temperature 212 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..