Polymer Property : Specific Heat Capacity = 0.111 BTU/lb-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Specific Heat Capacity	0.465 J/g-Â°C @Temperature 300 Â°C	0.111 BTU/lb-Â°F @Temperature 572 Â°F
Haynes HastelloyÂ® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649Â°C (1200Â°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Specific Heat Capacity	0.463 J/g-°C @Temperature 23.0 °C	0.111 BTU/lb-°F @Temperature 73.4 °F
Carpenter Thermo-Span® Fe-Co-Ni Superalloy Data provided by Carpenter Technology Corporation.Thermo-Span® alloy is a precipitation hardenable superalloy which exhibits a low coefficient of thermal expansion over a broad temperature range, h..
Specific Heat Capacity	0.465 J/g-°C @Temperature 300 °C	0.111 BTU/lb-°F @Temperature 572 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..
Specific Heat Capacity	0.465 J/g-°C @Temperature 300 °C	0.111 BTU/lb-°F @Temperature 572 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..
Specific Heat Capacity	0.465 J/g-°C @Temperature 300 °C	0.111 BTU/lb-°F @Temperature 572 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Specific Heat Capacity	0.465 J/g-°C @Temperature 300 °C	0.111 BTU/lb-°F @Temperature 572 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..