Polymer Property : CTE, linear, Parallel to Flow = 33.0 µm/m-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	33.0 µm/m-°C @Temperature -40.0 - 40.0 °C	18.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
CTE, linear, Parallel to Flow	33.0 µm/m-°C @Temperature -40.0 - 40.0 °C	18.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific) LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
CTE, linear, Parallel to Flow	33.0 µm/m-°C @Thickness 2.00 mm, Temperature 25.0 °C	18.3 µin/in-°F @Thickness 0.0787 in, Temperature 77.0 °F
BASF Ultrason® KR 4113 PESU with 10/10% Carbon Fibers/Graphite and 10% PTFE Description: Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibers, graphite and PTFE powder, considerably improves Ultrason’s tribological properties. In addition, ..
CTE, linear, Parallel to Flow	33.0 µm/m-°C @Thickness 2.00 mm, Temperature 75.0 °C	18.3 µin/in-°F @Thickness 0.0787 in, Temperature 167 °F
BASF Ultrason® KR 4113 PESU with 10/10% Carbon Fibers/Graphite and 10% PTFE Description: Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibers, graphite and PTFE powder, considerably improves Ultrason’s tribological properties. In addition, ..