SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ASTM D792
1.61 g/cc
0.0582 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0021 cm/cm

@Time 86400 sec
0.0021 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0051 cm/cm

@Time 86400 sec
0.0051 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
ISO 527
148 MPa
21500 psi
ASTM D638
Tensile Strength, Yield 145 MPa
21000 psi
ISO 527
148 MPa
21500 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ISO 527
2.2 %
2.2 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ISO 527
2.2 %
2.2 %
ASTM D638
Tensile Modulus 12.93 GPa
1875 ksi
1 mm/min; ISO 527
13.78 GPa
1999 ksi
50 mm/min; ASTM D638
Flexural Strength 206 MPa
29900 psi
ASTM D790
216 MPa
31300 psi
ISO 178
Flexural Modulus 11.72 GPa
1700 ksi
ASTM D790
11.8 GPa
1710 ksi
ISO 178
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.91 J/cm
16.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 57.0 kJ/m²
27.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 22.0 J
16.2 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.52
0.52
ASTM D3702 Modified
Coefficient of Friction, Static 0.52
0.52
ASTM D3702 Modified
K (wear) Factor 260 x 10-8 mm³/N-M
129 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
18.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
33.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
18.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 146 °C
295 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
145 °C

@Thickness 3.20 mm
293 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 142 °C
288 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
140 °C

@Thickness 3.20 mm
284 °F

@Thickness 0.126 in
unannealed; ASTM D648
Copyright © lookpolymers.com All Rights Reserved