Polymer Property : Thermal Conductivity = 25.1 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	25.1 W/m-K @Temperature 871 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 1600 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	25.1 W/m-K @Temperature 871 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 1600 Â°F
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	25.1 W/m-K @Temperature 871 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 1600 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	25.1 W/m-K @Temperature 871 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 1600 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	25.1 W/m-K @Temperature 871 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 1600 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	25.1 W/m-K @Temperature 871 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 1600 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	25.1 W/m-K @Temperature 427 Â°C	174 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Latrobe Viscount 44Â® Prehardened Tool Steel (ASTM H13S) Viscount 44 is a free-machining, prehardened, H13-type hot work tool steel. It is produced using special melting, forging, and heat treating processes which provide the optimum in control and reprod..
Thermal Conductivity	25.1 W/m-K @Temperature 93.0 °C	174 BTU-in/hr-ft²-°F @Temperature 199 °F
Crucible Steel 416R Chromium Stainless Steel Crucible 416R is a pre-hardened chromium stainless steel which is suitable for use in precision match-grade rifle barrels. It can be supplied in various hardness ranges according to the specific req..
Thermal Conductivity	25.1 W/m-K @Temperature 600.0 °C	174 BTU-in/hr-ft²-°F @Temperature 1112 °F
AK Steel 13-4 SR® Ferritic Stainless Steel AK Steel 13-4 SR Stainless Steel is a ductile weldable ferritic with 13% Cr and 3.75% Al. The high aluminum content results in a base alloy with high electrical resistivity. It is intended for use w..
Thermal Conductivity	25.1 W/m-K @Temperature 871 °C	174 BTU-in/hr-ft²-°F @Temperature 1600 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..